정헌생 한국자원공학회 2016 한국자원공학회지 Vol.53 No.6
The metallurgical processing to recover valuable metals from deep-sea manganese nodules has been developed in the past four decades. In the early days of the development, the recovery of three metals such as Cu, Ni, and Co was favored, but later four metals process including Mn was recognized more advantageous due to the economic and environmental concerns. Recently, research extends to the recovery of metals such as Mo, V, Zr and rare earth from nodules. In Korea, the smelting-sulfuric acid leach process is considered to be the most promising technology, and a continuous system with 200 kg/day capacity was successfully tested. 심해저 망간단괴로부터 유용금속을 회수하기 위하여 개발하여 온 제련기술들에 대하여 조사하고 기술 발전동향을 파악하고자 하였다. 제련기술은 구리, 니켈, 코발트의 3가지 금속을 회수하는 공정과 상기한 3가지 금속 외에망간을 추가한 4가지 금속을 회수하는 공정으로 크게 분류되는데, 개발 초기에는 3가지 금속의 회수가 선호되었으나, 근래에는 경제적․ 환경적인 이유로 4가지 금속의 회수가 대세가 되고 있다. 또한 금속의 분리기술이 발전하고, 수요가 급증함에 따라 최근에는 4가지 금속 외에도 망간단괴가 함유하고 있는 몰리브덴, 바나듐, 지르코늄과 같은 중요 금속과 이트륨, 탈륨과 같은 희토류 금속들의 회수에 주목하기 시작하였다. 우리나라는 용융-황산침출 공정을 상용화에유리한 기술로 판단하고, 200 kg/day 규모의 연속 통합시스템을 활용하여 실증실험을 수행하였고, 상용화 플랜트 설계를 위한 기반을 구축하고 있다.
Status of Discarded Home Electric Appliances Treatment
정헌생,오중환,황연,조영수,Chung, H. S.,Oh, J. H.,Hwang, Y.,Cho, Y. S. The Korean Institute of Resources Recycling 1994 資源 리싸이클링 Vol.3 No.2
발생량이 급증추세에 있어, 이들의 처리가 심각한 사회문제로써 대두되고 있는, 대형 폐가전제품에 대한 발생량 추이, 구성재료, 회수 및 재활용에 대한 국내현황에 대하여 기술하였다. Rapid increases of bulky home electric appliances such as televisions, refrigerators, washing machines, etc are about to create many problems in their waste management in Korea. This paper summarizes the present status of the discarded appliances treatment including the estimations of their quantity, constituent materials, and recyclings.
정헌생(Hun S. Chung) 한국태양에너지학회 1991 한국태양에너지학회 논문집 Vol.11 No.1
화석에너지로 부터 방출되는 온실효과 가스와 지구온난화 현상에 대하여 조사하였다. 세계의 사회경제활동과정에서 가속화가 예상되는 에너지 수요증가에 대응하기 위하여, 온실가스 배출을 감소시킬 화석에너지 이용시스템과 핵에너지와 청정자원인 재생에너지를 포함한 종합적인 에너지공급시스템개념에 대하여 고찰하였다. The greenhouse gases from fossil fuels and the global warming are discussed. In addition, a total clean energy system is conceptualized including the nuclear and renewable energies into a fossil fuel conversion stream to maintain the clean global environment while the increased energy demand, is fulfilled.
김동진,정헌생,이재천,김인회,이자현,Kim, Dong-Jin,Jeong, Heon-Saeng,Lee, Jae-Cheon,Kim, In-Hoe,Lee, Ja-Hyeon 한국재료학회 2000 한국재료학회지 Vol.10 No.3
마그네슘 함수 규산염인 사문석으로부터 염산침출하여 얻은 다공성의 침출잔사를 실리카원으로 사용하였다. ZSM-5 제올라이트는 사문석 침출잔사와 알루미늄원인 수산화 알루미늄을 각각 수산화나트륨에 혼합 용해하여 고온고압반응기를 사용하여 수열반응에 의하여 합성하였다. 반응온도와 반응시간, 알칼리 농도 및 하소온도 등을 변화시키며 실험을 행하였으며, 반응온도 $170^{\circ}C$, 반응시간 24시간, 조성 $11.7Na_2O{\cdot}Ai_2O_3{\cdot}90SiO_2{\cdot}3510H_2O{\cdot}10.8(TPA)_2O$ 그리고 하소온도 $600^{\circ}C$, 3시간에서 가장 높은 결정화도를 갖는 ZSM-5 제올라이트를 합성하였다. A serpentine mineral was treated in hydrochloric acid solution to obtain amorphous silica residue with high surface area. The highly porous silica with aluminum hydroxide and sodium hydroxide was hydrothermally reacted in an autoclave. A numerous experiments were performed in terms of reaction time, temperature, alkalinity, and calcinations temperature. As a result, a ZSM-5 zeolite of the highest crystallinity was produced under such conditions as $^170{\circ}C$ of the reaction temperature, 24 hours of the reaction time, and $11.7Na_2O{\cdot}Al_2O_3{\cdot}90SiO_2{\cdot}3510H_2O{\cdot}10.8(TPA)_2O$ the composition along with 3 hours of the calcinations at $600^{\circ}C$.
Li2O-Al2O3-SiO2계 결정화 유리의 특성(I)
양준환,정헌생 한국세라믹학회 1988 한국세라믹학회지 Vol.25 No.5
The properties of scid-resistance to boiling HCl, thermal expansion coefficient and softening temperature of mother glass and glass-ceramic of LAS systems were investigated at the contents of SiO2 varing from 57 to 67wt%. The nucleation and growth of crystalline phase of LAS compositions were carried out at 50$0^{\circ}C$ and $700^{\circ}C$. The crystalline phase jconsists of lithium alumino silicate, lithum meta silicate, lithium disilicate, $\alpha$-crystobalite and $\alpha$-quartz. Lithium alumino silicate(virgilite) is the major crystalline phase in the glass ceramics. The degree of acid resistant property was increased in proportion with the silica content for both glass and ceramics. Glass-ceramic gives lower acid-resistance and thermal expansion coefficient while softening temperature shows higher for glass-ceramic than for mother glass.
미립 코발트분말 합성을 위한 polyol공정에서 비균질계 핵생성 반응
김동진,정헌생,우상덕,이재장,안종관 한국결정성장학회 2002 한국결정성장학회지 Vol.12 No.2
코발트, 니켈, 구리 그리고 귀금속분말에 적용할 수 있는 polyol법은 균질한 크기와 형상을 갖는 금속분말합성에 매우 효과적인 공정이다 이 때 polyol은 용매, 환원제 그리고 보호제의 역학을 한다 $AgNO_3$글 촉매제로 첨가하여 비균질계 핵생성 반응을 야기할 경우 서브마이크폰 크기(0.5$\mu$m)의 코발트 분말을 한성학 수 있었다. 또한 촉매제인 Ag 핵의 수출 변화시키므로써 코발트 분말의 입도를 제어할 수 있음을 확인하였다. The polyol process which applies to cobalt, nickel. copper and precious metals is a interesting and unexpected example of such a method for preparing uniform metal powders. The reaction proceeds via dissolution, and the polyol acts simultaneously as a solvent, a reducing agent, and to some extent a protective agent. Submicrometer uniform cobalt particles can be obtained by seeding the reactive medium ($AgNO_3$) to achieve a complete substitution of homogeneous by heterogeneous nucleation. By varying the number of nuclei it is possible to control to some extent the average particle size in the submicrometer (0.5$\mu$m) range.