ZPCCY계 바리스터 세라믹스의 DC 가속열화 특성에 미치는 냉각속도의 영향

남춘우,김향숙 한국전기전자재료학회 2002 전기전자재료학회논문지 Vol.15 No.9

The microstructure, V-Ι characteristics, and stability of ZnO-P $r_{6}$ $O_{11}$ CoO-C $r_2$ $O_3$- $Y_2$ $O_3$-based varistor ceramics were investigated with cooling rate in the range of 2~8$^{\circ}C$/min. The cooling rate relatively weakly affected the microstructure, the varistor voltage, and the leakage current in the V-Ι characteristics. But the nonlinear exponent relatively strongly affected by cooling rate. The cooling rate also greatly affected the stability of V-Ιand dielectric characteristics for DC accelerated aging stress. On the whole, the varistors cooled with 4$^{\circ}C$/fin exhibited the highest performance in the densification, nonlinearity, and stability. Especially, they exhibited a high stability, in which the variation rate of the varistor voltage( $V_{1㎃}$), the nonlinear exponent($\alpha$), and the dissipation factor(tan $\delta$) is -1.4%, -4.9%, and +60.0%, respectively, under DC accelerated aging stress such as 0.95 $V_{1㎃}$15$0^{\circ}C$/12 h)

Zn-Pr-Co-Cr-Dy 산화물계 바리스터 세라믹스의 전기적 안정성

남춘우,박종아,김명준,류정선 한국세라믹학회 2003 한국세라믹학회지 Vol.40 No.11

Zn-Pr-Co-Cr-Dy 산화물계로 구성된 바리스터 세라믹스의 전기적 안정성을 몇 가지 DC 가속열화 스트레스 조건하에서 0.0∼2.0 mol% Dy$_2$O$_3$ 첨가량의 변화에 따라 조사하였다. 바리스터 세라믹스의 밀도는 Dy$_2$O$_3$ 첨가량이 0.5 mol%까지 증가하였으며, 보다 많이 첨가하면 감소하는 것으로 나타났다. 밀도는 전도경로와 밀접한 관계로 인해서 안정성에 큰 영향을 미치는 것으로 나타났다. Dy$_2$O$_3$ 첨가는 바리스터 세라믹스의 비직선 지수를 45 이상, 누설전류를 대략 1.0 $\mu$A 이하로 비직선성을 크게 개선시켰다. DC 스트레스 조건 0.95 V$_{1mA}$/15$0^{\circ}C$/24 h에서 안정성을 조사한 결과, 0.5 mol% 첨가시 상대적으로 가장 높은 안정성을 나타내었다. 전압-전류특성에 있어서 바리스터 전압, 비직선 지수, 누설전류의 변화율은 각각 -0.9%, -14.4%, +483.3%이었으며, 유전특성에 있어서 비유전율 및 손실계수의 변화는 각각 +7.1%, +315.4%이었다. 그 외의 바리스터 세라믹스는 낮은 밀도 때문에 열폭주 현상을 나타내는 매우 불안정한 특성을 나타내었다.다. The electrical stability of the varistor ceramics composed of Zn-Pr-Co-Cr-Dy oxides-based varistors was investigated at 0.0∼2.0 mol% Dy$_2$O$_3$ content under DC accelerated aging stress. The ceramic density was increased up to 0.5 mol% Dy$_2$O$_3$ whereas further addition of Dy$_2$O$_3$ decreased sintered ceramic density. The density sailently affected the stability due to the variation of conduction path. The nonlinearity of varistor ceramics was greatly improved above 45 in the nonlinear exponent and below nearly 1.0 ${\mu}$A by incorporating Dy$_2$O$_3$. Under 0.95 V$\_$1mA/150$^{\circ}C$/24 h stress state, the varistor ceramics doped with 0.5 mol% Dy$_2$O$_3$ exhibited the highest electrical stability, in which the variation rates of varistor voltage, nonlinear exponent, and leakage current were -0.9%, -14.4%, and +483.3%, respectively. The variation rates of relative permittivity and dissipation factor were +7.1% and +315.4%, respectively. The varistors with further addition of Dy$_2$O$_3$ exhibited very unstable state resulting in the thermal runaway due to low density.

소결시간에 따른 ZPCCD계 바리스터의 전기적 특성 및 안정성

남춘우,박종아,유대훈,서형권,Nahm, Choon-Woo,Park, Jong-Ah,Yoo, Dea-Hoon,Suh, Hyoung-Kwon 한국세라믹학회 2005 한국세라믹학회지 Vol.42 No.7

The electrical properties and stability of the varistors composed of ZnO-Pr$_{6}$O$_{11}$-CoO-Cr$_{2}$O$_{3}$-Dy$_{2}$O$_{3}$ system were investigated with sintering time in the range of 1$\~$3 h at 1350$^{\circ}C$ . As the sintering time was increased, the varistor voltage and leakage current increased, but the nonlinear exponent decreased. The varistors sintered for 1 h exhibited excellent nonlinearity, with a nonlinear exponent of 55.3 and a leakage current of 0.1 $\mu$A, whereas presented relatively low stability. The varistors sintered for 2 h exhibited not only high nonlinear exponent of 46.3, low leakage current of 0.3 $\mu$A, low dielectric dissipation factor of 0.0431, but also the highest stability, in which the variation rates of varistor voltage, nonlinear exponent, leakage current, dielectric constant, and dielectric dissipation factor were -3.0$\%$, -4.1$\%$, +3056.2$\%$, +5.1$\%$, and -12.5$\%$, respectively, after DC accelerated aging stress state of 0.95 V$_{1ma}$/150$^{\circ}C$/24 h. On the whole, the nonlinearity and stability of these varistors are greatly affected by the sintering time.

ZPCCY계 바리스터의 열화특성에 미치는 소결시간의 영향

남춘우,박종아 한국세라믹학회 2004 한국세라믹학회지 Vol.41 No.6

ZnO-P $r_{6}$ $O_{11}$-CoO-C $r_2$ $O_3$- $Y_2$ $O_3$계 세라믹스로 구성된 ZPCCY계 바리스터의 소결시간별 DC 가속열화 스트레스에 대한 전기적 안정성을 조사하였다. 소결시간은 전기적 특성 및 안정성에 크게 영향을 미치는 것으로 나타났다. 소결시간이 증가함에 따라 비직선 지수는 51.2∼23.8의 범위로 감소하였으며, 누설전류는 1.3∼5.6 $\mu$A의 범위로 증가하였다. 1시간 소결된 바리스터는 비직선성은 우수하나 밀도가 낮은 관계로 안정성이 상대적으로 낮았으며, 3시간 소결된 바리스터는 안정성은 양호하나 비직선성이 다소 낮은 것으로 나타났다 2시간 소결된 바리스터는 비직선 지수가 38.6, 누설전류가 3.6 $\mu$A로 양호 하고, DC스트레스_0.95 $V_{1㎃}$15$0^{\circ}C$/12h에서 바리스터 전압, 비직선 지수, 누설전류, 손실계수 변화율이 각각 -0.8%, -1.8%, +74.4%, +0.9%를 나타냄으로서 안정성이 우수한 것으로 나타났다.다. The electrical stability of ZPCCY-based varistors composing of ZnO-Pr$_{6}$O$_{11}$-CoO-C $r_2$ $O_3$- $Y_2$ $O_3$ ceramics were investigated in various DC accelerated aging stress with sintering times. Sintering time greatly affected electrical properties and stability. Sintering time decreased nonlinear exponent in the range of 51.2∼23.8 and increased leakage current in the range of 1.3∼5.6 ${\mu}$A. The varistor sintered for 1 h exhibited high nonlinearity, whereas relatively low stability. On the contrary, the varistor sintered for 3 h exhibited low nonlinearity, whereas relatively high stability. But the varistor sintered for 2 h exhibited not only good nonlinearity, with nonlinear exponent of 38.6 and leakage current of 3.6 ${\mu}$A but also high stability, in which the variation rates of varistor voltage, nonlinear exponent, leakage current, and dissipation factor are -0.80%, -1.81 %, +74.4%, and +0.88%, respectively.

Physicochemical stability, pharmacokinetic, and biodistribution evaluation of paclitaxel solid dispersion prepared using supercritical antisolvent process

Shanmugam, Srinivasan,Park, Jae-Hyun,Chi, Sang-Cheol,Yong, Chul Soon,Choi, Han-Gon,Woo, Jong Soo Informa Healthcare 2011 Drug development and industrial pharmacy Vol.37 No.6

<P><I>Aim:</I> To investigate the physicochemical stability, pharmacokinetics (PK), and biodistribution of paclitaxel (PTX) from paclitaxel solid dispersion (PSD) prepared by supercritical antisolvent (SAS) process.</P><P><I>Methods:</I> Physicochemical stability was performed in accelerated (40°째C 70 ??±짹 ??5% RH) and stress (60°째C) storage conditions for a period of 6 months and 4 weeks, respectively. PK and biodistribution studies were performed in rats following i.v. administration of PTX equivalent to 6 and 12 ??mg/kg formulations.</P><P><I>Results:</I> Physical stability of PSD showed excellent stability with no recrystallization of the amorphous form. Chemical stability of PSD in terms of % PTX remaining was 98.2 ??±짹 ??0.6% at 6 months and 97.9 ??±짹 ??0.3% at 4 weeks of accelerated and stress conditions, respectively. The PK study showed a nonlinear increase in AUC with increasing dose, that is, 100% increase in dose (from 6 to 12 ??mg/kg) resulted in 405.90% increase in AUC. Unlike PK study, the organ distribution study of PTX from PSD showed linear relationship with dose escalation. The order of organ distribution of PTX from highest to lowest for both PSD and Taxol<SUP>®짰</SUP> was liver>kidney>lung>brain.</P><P><I>Conclusions:</I> This study demonstrated excellent physicochemical stability with insight information on the PK and biodistribution of PTX from PSD prepared by SAS process.</P>

Dy₂O₃가 첨가된 ZPCCD계 바리스터의 DC 가속열화 특성

남춘우,박종아,김명준 한국전기전자재료학회 2003 전기전자재료학회논문지 Vol.16 No.12

The nonlinear properties and their stability of ZPCCD- based varistors, which are composed of ZnO P $r_{6}$ $O_{ll}$ - CoO-C $r_2$ $O_3$-D $y_2$ $O_3$-based ceramics, were investigated in the D $y_2$ $O_3$ content range of 0.0∼2.0 mol%. The incorporation of D $y_2$ $O_3$ greatly affected the nonlinear properties and the best nonlinearity was obtained from 0.5 mol% D $y_2$ $O_3$ with nonlinear exponent of 66.6 and leakage current of 1.2 $\mu$A. Further addition of D $y_2$ $O_3$ deteriorated the nonlinear properties. In stability against DC accelerated aging stress state: 0.95 $V_{1mA}$/15$0^{\circ}C$/24 h, the 0.5 mol% D $y_2$ $O_3$-doped varistor exhibited the highest stability, in which the variation rate of varistor voltage and nonlinear exponent are -1.9% and 10.5%, respectively. The remainder varistors resulted in thermal runaway due to low density of ceramics.s.s.

La₂O₃ Doped ZnO-Pr₆O₁₁계 바리스터 세라믹스의 전기적 성질 및 안정성

남춘우,Nahm, Choon-Woo 한국세라믹학회 2006 한국세라믹학회지 Vol.43 No.6

The varistor properties and DC accelerated aging characteristics of $ZnO-Pr_{6}O_{11}-CoO-Cr_{2}O_{3}$-based varistors were investigated at different $La_{2}O_3$ contents in the range of $0{\sim}2.0mol%$. The varistors doped with 0.5 mol% $La_{2}O_3$ exhibited good nonlinearity, with 81.6 in nonlinear coefficient. Increasing the $La_{2}O_3$ content further to 2.0 mol% caused the sintered density to increase, and the breakdown voltage and nonlinearity to decrease abruptly. The varistors with 0.5 mol% $La_{2}O_3$ exhibited the high electrical stability, with -1.14% in variation rate of breakdown voltage, -3.7% in variation rate of nonlinear coefficient, and +100% in variation rate of leakage current for specified DC accelerated aging stress condition (95% of breakdown voltage/$150^{\circ}C$/24 h).

ZPCCL계 세라믹스의 바리스터 특성

남춘우,Nahm, Choon-Woo 한국재료학회 2006 한국재료학회지 Vol.16 No.7

The varistor properties of ZPCCL-based ceramics were investigated at different $La_2O_3$ contents in the range of $0{\sim}2.0$ mol%. As $La_2O_3$ content increased, the ceramic density greatly increased in the range of $4.71{\sim}5.77\;g/cm^3$ and the varistor voltage greatly decreased in the range of $503.5{\sim}9.4$ V. The varistor with 0.5 mol% $La_2O_3$ exhibited good nonlinearity, in which the nonlinear exponent is 81.6 and the leakage current is 0.2 ${\mu}A$. Furthermore, the varistors exhibited the high electrical stability, with $%{\Delta}V_{1mA}=-1.1%,%{\Delta}{\alpha}=-3.7%$, and $%{\Delta}I_L=+100%$ for DC accelerated aging stress condition of 0.95 $V_{1mA}/150^{\circ}C/24$ h.

(Pr, Co, Cr)-doped ZnO 바리스터의 가속열화특성에 테르비아 첨가효과

남춘우,Nahm, Choon-Woo 한국전기전자재료학회 2007 전기전자재료학회논문지 Vol.20 No.6

The electrical properties and stability of $ZnO-Pr_6O_{11}-CoO-Cr_2O_3-based$ varistors were investigated for different $Tb_4O_{11}$ amounts in the range of $0{\sim}1.0\;mol%$. As the $Tb_4O_{11}$ amount increased, the sintered density increased in the range of $99.1{\sim}101.1%$ of theoretical density and the average grain size decreased in the range of $7.7{\sim}4.8{\mu}m$. The varistor voltage increased in the range of $280.9{\sim}715.8V/mm$ and the nonlinear coefficient increased in the range of $26.4{\sim}44.4$ with the increased of $Tb_4O_{11}$ amount. The 0.25 mol% $Tb_4O_{11}$-doped varistors exhibited the high electrical stability, with -0.1% in variation rate of varistor voltage, -0.7% in variation rate of nonlinear coefficient, and +17.4% in variation rate of leakage current for specified dc accelerated aging stress of $0.95V_{1mA}/150^{\circ}C/24h$.

코발트 산화물 첨가가 산화아연 바리스터의 전기적, 유전적 안정성에 미치는 영향

남춘우,유대훈,Nahm Choon-Woo,Yoo Dae-Hoon 한국재료학회 2005 한국재료학회지 Vol.15 No.11

The electrical and dielectric stability of zinc oxide-based varistors were investigated with the cobalt oxide contents in the range of $0.5\~5.0 mo\l%$. As cobalt oxide contents increased, the ceramic density increased in the range of $5.25\~5.55g/cm^3$ and the varistor voltage decreased in the range of $235.3\~86.0V$. The varistor with on addition of cobalt oxide $1.0 mol\%$ exhibited good nonlinearity. in which the nonlinear exponent is 66.6 and the leakage current is $1.2{\mu}A$. Furthermore, the varistors exhibited the highest electrical and dielectric stability, with $\%{\Delta}V_{1mA}=-1.9\%,\;\%{\Delta}{\alpha}=-10.5\%,\;\%{\Delta}I_L=+275.0\%,\;and\;\%{\Delta}tna{\delta}=+55.6\%$, under DC accelerated aging $0.95V_{1mA}/150^{\circ}C/24h$.