http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
Co<sub>3</sub>O<sub>4</sub> 첨가량 변화에 따른 ZnO Varistor의 전기적 특성
조현무,이성갑,Cho, Hyun-Moo,Lee, Sung-Gap 한국전기전자재료학회 2004 전기전자재료학회논문지 Vol.17 No.11
ZnO varistor ceramics which were fabricated with variation of added of 0.5~1.0 mol% Co$_3$O$_4$, were sintered at 1150 $^{\circ}C$. In the specimen added 0.7 mol% Co$_3$O$_4$, sintered density was 6.03 g/㎤ and electrical properties were superior to any other compositions. The nonlinear coefficient a and clamping voltage ratio were 83 and 1.35, respectively. But, endurance surge current in the specimen added 0.5 mol% Co$_3$O$_4$ was 7000 A/$\textrm{cm}^2$, and deviation of varistor voltage was Δ-3.23 %. As P.C.T and T.C.T environmental test were succeed in all specimens, and deviation of varistor voltage in the specimen added 0.6 mol% Co$_3$O$_4$ was Δ-0.81 %. All specimens showed good leakage current property on the High Temperature Continuous Load Test(HTCLT) for 1000 hr at 85 $^{\circ}C$ and variation rate of the varistor voltage below Δ-2.0 %.
Glass 첨가량에 따른 ZnO 바리스터의 전기적 특성
조현무,이종덕,박상만,이성갑,Cho, Hyun-Moo,Lee, Jong-Deok,Park, Sang-Man,Lee, Sung-Gap 한국전기전자재료학회 2005 전기전자재료학회논문지 Vol.18 No.9
ZnO varistor ceramics were fabricated with variation of addition of glass-frit amount and the sintering temperature was $1100^{\circ}C$. The average grain sizes were showed increased from $8.6{\mu}m\;to\;10{\mu}m$, and varistor voltages were decreased from 506V to 460V by added amount of glass-frit. Nonlinear coefficient $\alpha$, of all were with increasing the amount of glass-frit more than 70, in case of added on $0.03wt\%$ glass-frit was 83. And leakage current were less than $1{\mu}A$ with applied at $82\%$ of varistor voltage. The clamping voltage ratio of the specimens added $0.03wt\%$ glass-frit was 1.41 at applied 25A $[8/20\;{\mu}s]$. In the specimen added $0.03wt\%$ glass-frit, endurance of surge current and deviation of varistor voltage were $6200A/cm^2,\;\Delta-1.67\%$, respectively and clamping voltage ratio was 2.33. In the Specimen added $0.03wt\%$ glass-frit were superior to any other compositions on High Temperature Load Test(HTLT) for 1000 hr at $85^{\circ}C$, and deviation of the varistor voltage were $\Delta-1.29\%$.
이성갑,조현무,이종덕,박상만,Lee, Sung-Gap,Cho, Hyun-Moo,Lee, Jong-Deok,Park, Sang-Man 한국전기전자재료학회 2005 전기전자재료학회논문지 Vol.18 No.12
ZnO varistor ceramics added a glass-frit 0.03 $wt\%$ were fabricated with variation of sintering temperature. The sintering temperature and time were $1125^{\circ}C\~1200^{\circ}C$ and 2 h. The average grain sizes increased and the varistor voltage decreased with increasing the sintering temperature. The values of the specimen sintered at $1200^{\circ}C$ were $23.7\;{\mu}m$ and 329 V, respectively. The leakage current of all specimens was less than $1\;{\mu}A$ at DC $82\%$ of varistor voltage. The clamping voltage ratio of the specimen sintered at $1175^{\circ}C$ was 1.37. The endurance of surge current and the deviation of varistor voltage of the specimen sintered at $1175^{\circ}C$ were 6400 $A/cm^2$ and ${\Delta}-2.81\%$, respectively. After the High Temperature Load Test(HTLT) at $85^{\circ}C$ for 1000 h, the specimen sintered at $1175^{\circ}C$ showed the lowest deviation of varistor voltage of ${\Delta}-1.92\%$.