정우광,백구슬,윤미정,이지욱,Jung, Woo-Gwang,Back, Gu-Seul,Yoon, Mi-Jung,Lee, Jee-Wook 한국재료학회 2017 한국재료학회지 Vol.27 No.5
In this study, Fe-Ni slag, converter slag and dephosphorization slag generated from the steel industry, and fly ash or bottom ash from a power plant, were mixed at an appropriate mixing ratio and melted in a melting furnace in a mass-production process for glass ceramics. Then, glass-ceramic products, having a basalt composition with $SiO_2$, $Al_2O_3$, CaO, MgO, and $Fe_2O_3$ components, were fabricated through casting and heat treatment process. Comparison was made of the samples before and after the modification of the process conditions. Glass-ceramic samples before and after the process modification were similar in chemical composition, but $Al_2O_3$ and $Na_2O$ contents were slightly higher in the samples before the modification. Before and after the process modification, it was confirmed that the sample had a melting temperature below $1250^{\circ}C$, and that pyroxene and diopside are the primary phases of the product. The crystallization temperature in the sample after modification was found to be higher than that in the sample before modification. The activation energy for crystallization was evaluated and found to be 467 kJ/mol for the sample before the process modification, and 337 kJ/mol for the sample after the process modification. The degree of crystallinity was evaluated and found to be 82 % before the process change and 87 % after the process change. Mechanical properties such as compressive strength and bending strength were evaluated and found to be excellent for the sample after process modification. In conclusion, the samples after the process modification were evaluated and found to have superior characteristics compared to those before the modification.
정우광,권오덕,조문규,Jung, Woo-Gwang,Kwon, Oh-Duck,Cho, Mun-Kyu 한국재료학회 2009 한국재료학회지 Vol.19 No.9
In order to provide the mechanism of nozzle clogging, recovered nozzles for high strength steel grade were examined carefully after continuous casting. The thickness of clogged material in SEN is increased in the following order: from the bottom to the top of the nozzle, upper part of slag line, and the pouring hole. Nozzle clogging material begins to form due the adhesion of metal to nozzle wall, the decarburization, and reduction of oxide in the refractory by Al and Ti in the melt. The reduction of oxide in the refractory by Al and Ti improves the wettability of the melt on the refractory and forms a thin Al-Ti-O layer. Metal containing micro alumina inclusions is solidified on the Al-Ti-O layer, and the solid layer grows due to the heat evolution through the nozzle wall. Thermodynamic calculation has been made for the related reactions. The effect of superheat to the nozzle clogging is discussed on ultra low carbon steel and low carbon steel.
유기금속기상증착법에 의한 InGaN/GaN 양자점 구조의 성장거동
정우광,장재민,최승규,김진열,Jung, Woo-Gwang,Jang, Jae-Min,Choi, Seung-Kyu,Kim, Jin-Yeol 한국재료학회 2008 한국재료학회지 Vol.18 No.10
Growth behavior of InGaN/GaN self-assembled quantum dots (QDs) was investigated with respect to different growth parameters in low pressure metalorganic chemical vapor deposition. Locally formed examples of three dimensional InGaN islands were confirmed from the surface observation image with increasing indium source ratio and growth time. The InGaN/GaN QDs were formed in Stranski-Krastanow (SK) growth mode by the continuous supply of metalorganic (MO) sources, whereas they were formed in the Volmer-Weber (V-W) growth mode by the periodic interruption of the MO sources. High density InGaN QDs with $1{\sim}2nm$ height and $40{\sim}50nm$ diameter were formed by the S-K growth mode. Dome shape InGaN dots with $200{\sim}400nm$ diameter were formed by the V-W growth mode. InN content in InGaN QDs was estimated to be reduced with the increase of growth temperature. A strong peak between 420-460 nm (2.96-2.70 eV) was observed for the InGaN QDs grown by S-K growth mode in photoluminescence spectrum together with the GaN buffer layer peak at 362.2 nm (3.41 eV).
소결체와 저탄소강의 레이저용접 특성에 미치는 입열량 및 용접부 성분변화의 영향
정우광,조남준,김성욱,이창희,김승대,이주형,박화수,Jung Woo-Gwang,Cho Nam-Joon,Kim Sung-Wook,Lee Chang-Hee,Kim Sung-Dea,Lee Joo-Hyung,Park Hwa-Soo 한국재료학회 2004 한국재료학회지 Vol.14 No.6
A laser welding was applied between sintered tip of Fe-Co-W and low carbon steel shank for the diamond saw blade. The welding characteristics and formation of defects were investigated carefully for the weld fusion zone in different welding condition. Dendrite arm spacing in weld bead decreased with decrease of heat input. Co and W increased and Fe decreased in the weld fusion zone with increase of the heat input. The corresponding change of composition was observed with the change of beam position. The maximum and total length of crack decreased with increase of the heat input. The crack in weld bead was propagated along the dendrite boundary and was caused mainly by the segregation of constituent during the solidification.
기전력법에 의한 용융 ZR-(In, Sn) 합금의 활동도 측정
정우광,Jung Woo-Gwang 한국재료학회 2005 한국재료학회지 Vol.15 No.1
The E.M.F. of the galvanic cell with fused salt was measured to determine the activities of zinc at 720-860 K over the entire composition range of liquid Zn-In and Zn-Sn alloys. The cell used was as follows: $$(-)W{\mid}Zn(pure){\mid}Zn^{2+}(KCl-LiCl){\mid}Zn(in\;Zn-In\;or\;Zn-Sn\;alloy){\mid}W(+)$$ The activities of zinc in the alloys showed positive deviation from Raoult's law over the entire composition range. The activity of cadmium and some thermodynamic functions such as Gibbs free energy, enthalpy and entropy were derived from the results by the thermodynamic relationship. The comparison of the results and the literature data was made. The liquid Zn-In and Zn-Sn alloys are found to be close tn the regular solution. The concentration fluctuations in long wavelength limit, $S_{cc}(o)$, in the liquid alloy were calculated from the experimental results.
정우광,김병수,이재천,Jung, Woo-Gwang,Kim, Byung-Soo,Lee, Jae-Chun 한국재료학회 2011 한국재료학회지 Vol.21 No.12
With an increased production of Printed Circuit Boards (PCBs) in electronic equipment, the consumption of solder alloys is growing globally. Recently, increasing importance of recycling solder scrap has been recognized. Generally, solder scrap contains many impurities such as plastics and other metals. Hazardous components must be eliminated for recycling solder scrap. The present work studied pretreatment for reuse of solder scrap alloys. An experiment was conducted to enhance the cleanliness of solder scrap melt and eliminate impurities, especially lead. Physical separation with sieving and magnetic force was made along with pyrometallurgical methods. A small decrease in lead concentration was found by high temperature treatment of solder scrap melt. The impurities were removed by filtration of the solder scrap melt, which resulted in improvement of the melt cleanliness. A very low concentration of lead was achieved by a zone melting treatment with repeated passage. This study reports on a pretreatment process for the reuse of solder scrap that is lead free.
소결체와 저탄소강의 레이저용접시 생성되는 캐비티의 형성과 용접 특성에 대한 연구
조남준,정우광,김성욱,이창희,김승대,Cho Nam-Joon,Jung Woo-Gwang,Kim Sung-Wook,Lee Chang-Hee,Kim Sung-Dea 한국재료학회 2004 한국재료학회지 Vol.14 No.4
A laser welding has been made between sintered tip of Fe-Co-W and low carbon steel shank for the diamond saw blade. The welding characteristics and formation of defect has been investigated carefully for the weld fusion zone in different welding condition. Full penetration has been observed for the whole range of heat input investigated in the present work. Bead width and under-fill have been increased with the increase of heat input. With increasing of heat input small cavities were decreased while large cavities were increased. The ratio of total cavity area to the entire weld bead area was not changed significantly with change of heat input. Most of cavities were found near the tip, and supposed to be formed from the pore in the tip.
지상탱크의 부식감지를 위한 음향방출시험에서 발생한 전자기간섭신호의 특성 연구
김승대,정우광,Kim, Sung-Dai,Jung, Woo-Gwang 한국재료학회 2007 한국재료학회지 Vol.17 No.5
The evaluation and comparison have been made for the EMI noise which was included in the signal from the sensors in the acoustic emission testing for the bottom plate of ground tank at full. The EMI signal has been classified into two types. One is the signal with very short AE count, and this signal possibly can be filtered by front end filter setting of the channel count with low level of 4 and high level of $10^8$. The other EMI signal occurred from CH 1, CH 3 and CH 10, and had high and constant duration with high energy and count (maximun duration > $10^5\;{\mu}s$), and has characteristic gradient of accumulation amplitude distribution. This signal should be removed in the AE signal evaluation by filtering, because this may affect to the total gradient.
유동법에 의한 용융 ZnCl<sub>2</sub> 및 FeCl<sub>2</sub>의 증기압 측정
이우상,김원용,정우광,Lee, Woo-Sang,Kim, Won-Yong,Jung, Woo-Gwang 한국재료학회 2010 한국재료학회지 Vol.20 No.3
Chloride-based fluxes such as NaCl-KCl are used in the refining of Al melt. The vapor pressure of the chloride is one of the fundamental pieces of information required for such processes, and is generally high at elevated temperatures. In order to measure the vapor pressure for chlorides, the apparatus for the transpiration method was assembled in the present study. The vapor pressure of $ZnCl_2$ and $FeCl_2$, which is related with the process of aluminum refining and the recovery of useful elements from iron and steel industry by-products, was also measured. In the measurement of vapor pressure by the transpiration method, the powder of $ZnCl_2$ or $FeCl_2$ in a alumina boat was loaded in the uniform zone of the furnace with a stream of Ar. The weight loss of $ZnCl_2$ and $FeCl_2$ after holding was measured by changing the flow rate of Ar gas (10 sccm -230 sccm), and the partial pressures of $ZnCl_2$ and $FeCl_2$ were calculated. The partial pressures within a certain range were found to be independent of the flow rate of Ar at different temperatures. The vapor pressures were measured in the temperature range of 758-901K for $ZnCl_2$ and 963-983K for $FeCl_2$. The measured results agreed well with those in the literature.