Naphthoquinone -1,2- Diazaide - Sulfonyl 기 치환 Polysiloxane 의 합성과 그 감광특성
강두환,정낙진 ( Doo Whan Kang,Nag Jin Chung ) 한국공업화학회 1991 공업화학 Vol.2 No.4
Hexamethylcyclotrisiloxane (D_3), tetramethylcyclotetrasiloxane (TMCTS)을 공중합 시켜 Si-H 결합을 함유한 polysiloxane 공중합체를 합성하고 allylamine과 반응시켜 amino기를 도입시킨 후 naphthoquinone-1,2-diazide-5-sulfonyl chlorde 와 반응시켜 naphthoquinone-1,2-diazide-5-sulfonyl 기가 도입된 polysiloxane 을 합성하였다. 생성 공중합체의 열적특성을 측정한 결과, 열분해온도는 360∼450 ℃ 정도였으며 또한 감광특성은 backbone 수지의 분자량이나 증감제의 종류에 따라 영향을 받았다. Sensitivity는 50∼120 mJ/㎠였고 contrast(γ)는 1.4∼2.1였으며 backbone 수지의 분자량이 증가함에 따라 약간 감소하였다. Polysiloxane copolymers were prepared by copolymerizing hexamethylcyclotrisiloxane with tetramethylcyclotetrasiloxane, and then reacted with allyamine. Copolymers containing naphthoquinone-1,2-diazide-5-sulfonyl group were synthesized by reacting naphthoquinone-1,2-diazide-5-sulfonyl chloride with siloxane copolymers having amino group. Thermal decomposition temperatures of copolymers were 360∼450 ℃, and photosensitive characteristics were dependent on the molecular weights of backbone resins and sensitizers. Sensitivity of copolymers was 50-120 mJ/㎠ and contrast (γ) was 1.4∼2.1.
Poly ( methylpheny ) Silane Photoresist 의 특성
강두환,정낙진 ( Doo Whan Kang,Nak Jin Chung ) 한국공업화학회 1990 공업화학 Vol.1 No.2
Polymethylphenylsilane(PMPS) was synthesized with methylphenyldichlorosilane using metal sodium. Various sample coated on quartz plate were exposed and the yield of residual film was calculated. To obtain the fine image forming after developing and drying, optical transmittance characterization have to be considerd. Exposure is described by three optical paramerters X, Y, and Z. There parameters are normally determined from optical transmittance measurements of exposed PMPS films. Z parameter was determined from the initial slope of a transmittance according to exposure time. This set of function parameters provided a complete description of photoresist exposure and development and became the basis for the theoretical process models.
Polyoxyethylene glycol fatty acid ester 계 유분산제의 제조와 Weathering Crude Oil 에 대한 분산효율 특성
염규설,강두환,김원기,정낙진,황재욱 ( Kuy Seol Yeom,Doo Whan Kang,Won Ki Kim,Nak Jin Chung,Jae Wook Whang ) 한국유화학회 1998 한국응용과학기술학회지 Vol.15 No.3
Polyoxyethylene monooleate was prepared by addition of ethylene oxide to oleic acid. And also, polyoxyethylene monooleate type oil dispersant was prepared by blending polyoxyethylene monooleate, n-paraffine, sorbitan monooleate, sorbitan monopalmitate, and plam oil. Dispersion efficiency test was carried out by vertical shaking flask and swirling flask methods. Low toxic oil dispersant was prepared with polyoxyethylene monooleate, which has high biodegradability and excellent dispersion efficiency on crude oils and weathered W/O emulsions with high viscosity, and its dispersion efficiency was measured to various crude oils and weathered oils.
내가수분해성 Polyester Polyol 을 이용한 Polyurethane 발포탄성체의 합성과 특성
이승훈,강두환,김영민,권동건,정낙진 한국공업화학회 1998 응용화학 Vol.2 No.2
Polyurethane (PU) foam elastomer prepared using polyester polyol has an excellent mechanical properties, but has the poor water proofness, compared with PU foam elastomer prepared using polyether polyol. PU foam elastomer was prepared by the reaction of NCO-prepolymer and polyester polyols obtained from 1,6-hexanediol (HD) and neopentyl glycol (NG) with adipic acid (AA). The water proofness of the elastomer was determined by measuring the change of mechanical properties of the elastomer according to hydrolytic degradation.