고에너지 볼밀링 방법에 의해 얻어진 초미립 AlN 분말의 치밀화 및 미세구조
박해룡,김영도,류성수,Park, Hae-Ryong,Kim, Young-Do,Ryu, Sung-Soo 한국분말야금학회 2012 한국분말재료학회지 (KPMI) Vol.19 No.1
In this study, a high energy ball milling process was employed in order to improve the densification of direct nitrided AlN powder. The densification behavior and the sintered microstructure of the milled AlN powder were investigated. Mixture of AlN powder doped with 5 wt.% $Y_2O_3$ as a sintering additive was pulverized and dispersed up to 50 min in a bead mill with very small $ZrO_2$ beads. Ultrafine AlN powder with a particle size of 600 nm and a specific surface area of 9.54 $m^2/g$ was prepared after milling for 50 min. The milled powders were pressureless-sintered at $1700^{\circ}C-1800^{\circ}C$ for 4 h under $N_2$ atmosphere. This powder showed excellent sinterability leading to full densification after sintering at $1700^{\circ}C$ for 4 h. However, the sintered microstructure revealed that the fraction of yitttium aluminate increased with milling time and sintering temperature and the newly-secondary phase of ZrN was observed due to the reaction of AlN with the $ZrO_2$ impurity.
직접질화법 AlN 분말의 소결거동 및 열전도도에 미치는 고에너지 볼밀링 효과
박해룡,김형태,이성민,김영도,류성수 한국세라믹학회 2011 한국세라믹학회지 Vol.48 No.5
In this study, a high energy ball milling process was introduced in order to improve the densification of direct nitrided AlN powder. The sintering behavior and thermal conductivity of the AlN milled powder was investigated. The mixture of AlN powder and 5 wt% Y_2O_3 as a sintering additive was pulverized and dispersed by a bead mill with very small ZrO_2 bead media. The milled powders were sintered at 1700℃-1800℃ for 4 h under N_2 atmosphere. The results showed that the sintered density was enhanced with increasing milling time due to the particle refinement as well as the increase in oxygen contents. Appropriate milling time was effective for the improvement of thermal conductivity, but the extensive millied powder formed more fractions of secondary phase during sintering,resulted in the decrease in thermal conductivity. The AlN powder milled for 10min after sintering at 1800℃ revealed the highest thermal conductivity, of 164W/m·K in tne densified AlN sintered at 1800℃.
임대주택정책의 평가 : 역사적 접근 Historical Approach
박해룡,이종열 한국행정사학회 2003 韓國行政史學誌 Vol.12 No.-
우리는 그러한 식민지유제를 청산하고 민족자립경제를 구축할 수 있는 계기가 있었음에도 불구하고 경제이익만을 추구하는 일부 자본가 세력이나 국가 민족의 장래보다 자신의 안일과 성장만을 추구하는 일부 관료들로 인해서 그 기회를 놓쳐 버리게 되었다. 또한 1960년대 이후 빈곤의 극복과 경제성장을 최대의 과제로 생각하여 추진하여 온 공화국정부의 경제정책은 양적인 면에서 상당한 경제적 성장을 가져왔음에도 불구하고 농업의 위축, 중소기업의 약화와 대기업의 거대화, 누적된 외채, 성장기반의 취약성 등 많은 문제성을 노출하고 있다. 물론 이러한 공화당정부의 정책에 대한 평가는 시기상조라는 견해도 없지 않다. 주류경제학의 논리에 따라 외자·수출주도형의 경제정책의 결과 성장을 이룩하였고 그 덕택에 오늘날 비교적 경제적 안정을 누릴 수 있으며 앞으로도 성장을 가져 올 것이라는 견해도 있다. 뿐만 아니라 다른 발전도상국가의 발전모형이 되고 있다고 평가되기도 한다. 그러나 성장이 양적인 것이며 질적인 면에서 그것은 농업문제, 심각한 왜채문제, 중소기업문제, 노동문제, 대외의존성문제 등 많은 항계성을 지니고 있다는 점이 지적되고 있다. 따라서 이와 같은 대외 의존적 경제체제를 극복하고 자립적 민족경제의 토대를 확립하는 방향에서 정책전환이 요구된다고 하겠다.