http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
휨하중을 받는 스마트 초고강도 섬유보강 콘크리트의 전기역학적 거동 조사
김태욱,김민경,김동주,Kim, Tae-Uk,Kim, Min-Kyoung,Kim, Dong-Joo 한국구조물진단유지관리공학회 2022 한국구조물진단유지관리공학회 논문집 Vol.26 No.5
This study investigated the electromechanical response of smart ultra-high performance fiber reinforced concretes (S-UHPFRCs) under flexural loading to evaluate the self-sensing capacity of S-UHPFRCs in both tension and compression region. The electrical resistivity of S-UHPFRCs under flexural continuously changed even after first cracking due to the deflection-hardening behavior of S-UHPFRCs with the appearance of multiple microcracks. As the equivalent bending stress increased, the electrical resistivity of S-UHPFRCs decreased from 976.57 to 514.05 kΩ(47.0%) as the equivalent bending stress increased in compression region, and that did from 979.61 to 682.28 kΩ(30.4%) in tension region. The stress sensitivity coefficient of S-UHPFRCs in compression and tension region was 1.709 and 1.098 %/MPa, respectively. And, the deflection sensitivity coefficient of S-UHPFRCs in compression region(30.06 %/mm) was higher than that in tension region(19.72 %/mm). The initial deflection sensing capacity of S-UHPFRCs was almost 50% of each deflection sensitivity coefficient, and it was confirmed that it has an excellent sensing capacity for the initial deflection. Although both stress- and deflection-sensing capacity of S-UHPFRCs under flexural were higher in compression region than in tension region, S-UHPFRCs are sufficient as a self-sensing material to be applied to the construction field.
제강 슬래그 잔골재가 혼입된 초속경 시멘트 기반 스마트 보수재료의 전기역학적 특성
김태욱,김민경,김동주,Tae-Uk Kim,Min-Kyoung Kim,Dong-Joo Kim 한국구조물진단유지관리공학회 2023 한국구조물진단유지관리공학회 논문집 Vol.27 No.4
This study investigated the electromechanical properties of cement based smart repair materials (SRMs) according to the different amounts of fine steel slag aggregates (FSSAs). SRMs can self-diagnose the quality of repairing and self-sense the damage of repaired zone. The replacement ratios of FSSAs to sand for SRMs were 0% (FSSA00), 25% (FSSA25), and 50% (FSSA50) by sand weight. The electrical resistivity of SRMs generally decreased as the compressive stress of SRMs increased: the electrical resistivity of FSSA25 at the age of 7 hours decreased from 78.16 to 63.68 kΩ-cm as the compressive stress increased from 0 to 22.37 MPa. As the replacement ratio of FSSAs by weight of sand increased from 0% to 25%, the stress sensitivity coefficient (SSC) of SRM at the age of 7 h increased from 0.471 to 0.828 %/MPa owing to the increased number of partially conductive paths in the SRMs. However, as the replacement ratio of FSSAs further increased up to 50%, the SSC decreased from 0.828 to 0.649 %/MPa because some of the partially conductive paths changed to continued conductive ones. SRMs are expected to self-sense the quality and future damage of repaired zone only by measuring the electrical resistivity of the repaired zone in addition to fast recovery in the mechanical resistance of structures.
불확실한 물성치를 갖는 복합재료 적층 평판의 파괴 예측
김태욱,신효철,Kim, Tae-Uk,Sin, Hyo-Cheol 대한기계학회 2000 大韓機械學會論文集A Vol.24 No.1
Because of their superior mechanical properties to isotropic materials, composite laminated plates are used for many structural applications that require high stiffness-to-weight and strength-to-weight ratios. Composite materials are always subject to a certain amount of scatter in their elastic moduli, but most analyses and designs with the materials are usually conducted by assuming that the material properties are fixed and have no uncertainties. In this paper, a convex modeling approach is introduced to take account of such uncertainties in elastic moduli. It is used with the finite element method to predict the onset of failures in composite laminated plates subject to in-plane loading. Numerical results show that failures begin at the smaller load when the uncertainties of elastic moduli considered and therefore, such uncertainties should be considered at the design stage for the safety and reliability of the structures.