산소-아세틸렌 토치의 조사각이 ZrB2-SiC UHTC 복합체 삭마 특성에 미치는 영향
이승용,공정훈,송정환,손영일,김도경 한국재료학회 2022 한국재료학회지 Vol.32 No.12
In this work, the ablation behavior of monolith ZrB2-30 vol%SiC (Z30S) composites were studied under various oxy-acetylene flame angles. Typical oxidized microstructures (SiO2/SiC-depleted/ZrB2-SiC) were observed when the flame to Z30S was arranged vertically. However, formation of the outmost glassy SiO2 layer was hindered when the Z30S was tilted. The SiC-depleted region was fully exposed to air with reduced thickness when highly tilted. Traces of the ablated and island type SiO2 were observed at intermediate flame angles, which clearly verified the effect of flame angle on the ablation of the SiO2 layer. Furthermore, the observed maximum surface temperature of the Z30S gradually increased up to 2,200 °C proving that surface amorphous silica was continuously removed while monoclinic ZrO2 phase began to be exposed. A proposed ablation mechanism with respect to flame angles is discussed. This observation is expected to contribute to the design of complex-shaped UHTC applications for hypersonic vehicles and re-entry projectiles.
탈규소화를 통한 LSI-Cf/SiC 복합재료의 내산화성 향상
송정환,공정훈,이승용,손영일,김도경 한국추진공학회 2022 한국추진공학회지 Vol.26 No.6
Cf/SiC 복합재는 저밀도, 높은 기계적 강도, 우수한 열 안정성을 가지고 있어 로켓 추진기관, 항공 및 군사 분야 등의 고온 응용 산업에 유망한 재료이다. 그러나 용융 실리콘 함침(Liquid Silicon Infiltration, LSI) 공정을 통해 제작된 복합재는 잔존하는 Si에 의하여 물리적, 열적 특성이 저하된다. 본 논문에서는 LSI 공정을 통해 제작된 Cf/SiC 복합재의 내부 Si을 제거하기 위한 방안으로 탈규소화(de-siliconization) 공정을 도입하였다. 최대 5분 동안 옥시아세틸렌 토치 테스트를 진행하고 시편의 산화된 표면과 단면은 3D scanning, X-ray diffraction(XRD), 광학현미경(OM), 전자주사현미경 (SEM)으로 분석하였다.