산화물계 SEN내화물의 슬래그 라인부 침식특성 연구 = Study on the Corrosion Characteristics in the Slag Line of SEN Oxide Refractory

다국어 초록 (Multilingual Abstract)

The corrosion resistance of submerged entry nozzle (SEN) materials were investigated for high-class steel manufacturing. Composite samples were fabricated by mixing $ZrO_2$, $Al_2O_3$, MgO, mullite, spinel, and carbon. The raw materials were mixed with attrition milling, compacted in a uniaxial pressure of 200MPa and calcined at $1000^{\circ}C$ for 3 h in $N_2$ atmosphere. The bulk density and apparent porosity of the calcined samples were measured by the liquid displacement method in water using Archimedes's principle. The corrosion resistance of the samples were measured by cup test with mold powder at $1550^{\circ}C$ for 2 h. The microstructure and elemental analysis of samples were observed by scanning electron microscopy (SEM), energy dispersive spectrum (EDS), and X-ray diffraction pattern (XRD). The XRD result shows that the starting raw materials were crystalline phase. The microstructure of fabricated specimen was investigated before and after corrosion tests at $1000^{\circ}C$ and $1550^{\circ}C$ for 2h. $ZrO_2$-C composite showed good resistance in the slag corrosion test. Among the composite oxide materials, $ZrO_2-Al_2O_3$-C and $ZrO_2$-MgO-C showed better resistance than $ZrO_2$-C in the slag corrosion test. The diameter variation index of $ZrO_2$-C refractory was 16.1 at $1000^{\circ}C$ for 2 h. The diameter variation index of the $ZrO_2-Al_2O_3$-C refractory was larger than that of the $ZrO_2$-C refractory at $1550^{\circ}C$ for 2 h.

참고문헌 (Reference)

1 K. Okamoto, 47 : 1982

2 D. Apelian,

3 A. W. Cramb,

4 R. V. Branion,

5 W. L. McCauley, 69 : 87-, 1986

6 M. K. Cho, 36 (36): 410-, 1999

7 G. J. Bayly,

8 I. S. Kim, 38 (38): 238-, 2001

9 S. Sunwoo, 10 (10): 226-, 2000

10 R. Stevens, "Zirconia and Zirconia Ceram" Magnesium Elektron Ltd 1986

11 천승호, "MgO-Carbon 내화물의 산화반응기구와 TiC 첨가에 의한 산화방지 효과" 한국세라믹학회 41 (41): 5-5, 2004

12 A. M. Alper, "High Temperature Oxides Part II" Academic press 5-, 1970