<P>Poly(N-isopropylacrylamide) (PNIPA)/silica composite hydrogels were prepared and the effects of the silica incorporation on the swelling and breaking characteristics of the hydrogels were investigated. To improve the dispersive property of si...
http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
https://www.riss.kr/link?id=A107627521
2008
-
SCOPUS,SCIE
학술저널
2439-2445(7쪽)
0
상세조회0
다운로드다국어 초록 (Multilingual Abstract)
<P>Poly(N-isopropylacrylamide) (PNIPA)/silica composite hydrogels were prepared and the effects of the silica incorporation on the swelling and breaking characteristics of the hydrogels were investigated. To improve the dispersive property of si...
<P>Poly(N-isopropylacrylamide) (PNIPA)/silica composite hydrogels were prepared and the effects of the silica incorporation on the swelling and breaking characteristics of the hydrogels were investigated. To improve the dispersive property of silica in the PNIPA matrix via the formation of covalent bonds between the polymer and silica, vinyl groups were introduced in the silica by reacting it with a coupling agent, 3-methacryloxypropyltrimethoxysilane. When unmodified silica was used as filler in the PNIPA-composite hydrogel, the swelling ratio of the composite hydrogel below the critical gel transition temperature (CGTT) increased with increasing silica content. However, when the modified silica was used as the filler, the swelling ratio below CGTT decreased with increasing silica content because of the enhanced distribution and additional crosslinking. Above CGTT, the swelling ratios of the PNIPA/silica hydrogels were similar regardless of the silica modification. The gel breaking stress of the hydrogels increased with increasing silica content, and this enhancement was larger for the modified silica hydrogel. Scanning electron microscopy images showed that the modified silica particles were distributed more evenly in the PNIPA matrix than the unmodified ones were and that the size of cell-like structure of the hydrogel decreased with increasing modified silica content. POLYM. ENG. SCI., 2008. © 2008 Society of Plastics Engineers</P>