In this work, we fabricated reduced large-area graphene oxide (rLGO) with maximum surface area of 1592μm<SUP>2</SUP> through a cost-effective chemical reduction process at low temperature. The product revealed large electrical conductiv...
http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
https://www.riss.kr/link?id=A107735721
Kumar, P. ; Shahzad, F. ; Yu, S. ; Hong, S.M. ; Kim, Y.H. ; Koo, C.M.
2015
-
SCOPUS,SCIE
학술저널
494-500(7쪽)
0
상세조회0
다운로드다국어 초록 (Multilingual Abstract)
In this work, we fabricated reduced large-area graphene oxide (rLGO) with maximum surface area of 1592μm<SUP>2</SUP> through a cost-effective chemical reduction process at low temperature. The product revealed large electrical conductiv...
In this work, we fabricated reduced large-area graphene oxide (rLGO) with maximum surface area of 1592μm<SUP>2</SUP> through a cost-effective chemical reduction process at low temperature. The product revealed large electrical conductivity of 243+/-12Scm<SUP>-1</SUP> and thermal conductivity of 1390+/-65Wm<SUP>-1</SUP>K<SUP>-1</SUP>, values much superior to those of a conventional reduced small-area graphene oxide (with electrical conductivity of 152+/-7.5Scm<SUP>-1</SUP> and thermal conductivity of 900+/-45Wm<SUP>-1</SUP>K<SUP>-1</SUP>). The rLGO thin film also exhibited not only excellent stiffness and flexibility with Young's modulus of 6.3GPa and tensile strength of 77.7MPa, but also an efficient electromagnetic interference (EMI) shielding effectiveness of ~20dB at 1GHz. The excellent performance of rLGO is attributed to the fact that the larger area LGO sheets include much fewer defects that are mostly caused by the damage of graphene sp<SUP>2</SUP> structure around edge boundaries, resulting in large electrical conductivity. The manufacturing process of rLGO is an economical and facile approach for the large scale production of highly thermally conducting graphene thin films with efficient EMI shielding properties, greatly desirable for future portable electronic devices.
Co9S8-carbon composite as anode materials with improved Na-storage performance