CsPbX$_3$ (X = Br, I) 양자점의 광학적 특성 = Optical Properties of CsPbX$_3$ (X = Br, I) Quantum Dots

다국어 초록 (Multilingual Abstract)

In order to investigate the photoluminescence (PL) and the X-ray excited luminescence (XEL) characteristics of CsPbBr$_3$ and CsPbI$_3$ quantum dots with high effective mass ($Z_{eff}$), we synthesized CsPbBr$_3$ and CsPbI$_3$ quantum dots with a cubic phase by using the wet chemical method. The CsPbBr$_3$ quantum dots had a PL peak at 522 nm and an XEL peak at 537 nm. The CsPbI$_3$ quantum dots had a PL peak at 690 nm and an XEL peak at 711 nm. The high XEL peaks could be attributed to the high $Z_{eff}$ of the CsPbBr$_3$ and the CsPbI$_3$ quantum dots (62.24 and 64.04, respectively). The high $Z_{eff}$ might have led to the high stopping power for X-ray detection. These results show the potential of CsPbBr$_3$ and CsPbI$_3$ quantum dots for applications in the field of optical and X-ray detection.

국문 초록 (Abstract)

높은 유효 질량($Z_{eff}$)을 가지는 CsPbBr$_3$와 CsPbI$_3$ 양자점의 광 발광 (photoluminescence, PL) 및 X-선 여기 발광 (X-ray emitted luminescence, XEL) 특성을 확인하기 위해 습식 화학법으로 크기가 각각 5 nm, 8 nm이고 입방 구조를 가지는 CsPbBr$_3$와 CsPbI$_3$ 양자점을 합성하였다. CsPbBr$_3$ 양자점은 522 nm에서 PL피크를, 537 nm에서 XEL 피크를 가지고, CsPbI$_3$ 양자점은 690 nm에서 PL피크를, 711 nm에서 XEL 피크를 가진다. CsPbBr$_3$와 CsPbI$_3$ 양자점의 높은 $Z_{eff}$(각각 62.24, 64.04)는 X-선 검출에 요구되는 높은 정지 전압을 야기하므로, 높은 XEL 스펙트럼 피크를 가지는 CsPbBr$_3$와 CsPbI$_3$ 양자점은 광 검출 및 X-선 검출 분야에 활용 가능성이 있다고 할 수 있다.

참고문헌 (Reference)

1 W. S. Yang, 348 : 1234-, 2015

2 L. Protesescu, 15 : 3692-, 2015

3 Q. A. Akkerman, 137 : 10276-, 2015

4 H. C. Wang, 55 : 7924-, 2016

5 R. C. Murty, 207 : 398-, 1965

6 S. Yakunin, 6 : 8056-, 2015

7 N. J. Jeon, 517 : 476-, 2015

8 M. Bruchez, 281 : 2013-, 1998

9 H. Zhang, 27 : 1604382-, 2017

10 A. Swarnkar, 354 : 92-, 2016