박판주조법으로 제조한 Al-0.6Mg-1.2Si 합금판재의 소부경화특성 = Bake-hardening Properties of Al-0.6Mg-1.2Si Alloy Sheets Fabricated by Twin Roll Casting

다국어 초록 (Multilingual Abstract)

The effect of pre-aging treatment on the microstructure and mechanical properties of Al-0.6Mg-1.2Si aluminum alloy sheets fabricated by twin roll casting (TRC) was investigated. It was observed that two kinds of nanoclusters, cluster(1) and cluster(2), play an important role in the bake-hardening properties of Al-Mg-Si aluminum alloy. The hardness of the TRC Al-0.6Mg-1.2Si alloy sheets was continuously increased up to 48 h by natural-aging, and the highest yield strength value was about 146 MPa. The yield strength was 280 MPa after bake-hardening at 180 ℃ for 30 min immediately after quenching, whereas the yield strength was 172 MPa when natural-aging proceeded for about 1 week before bake-hardening. This result is due to fact that cluster(1) is formed during natural-aging at room temperature and has detrimental effects on bake-hardening. On the other hand, when pre-aged at 150 ℃ for 10 min, cluster(2) predominantly formed and promoted the precipitation of β″ phase. The yield strength was 256 MPa after bake-hardening, which indicates that the pre-aging treatment is an effective method, and also depresses the negative effects of natural-aging and promotes β″ precipitation. The Al-Mg-Si aluminum alloy sheets fabricated by twin roll casting method exhibited mechanical properties equal to or higher than those of the direct-chill (DC) casting sheets despite the simplified manufacturing process.

참고문헌 (Reference)

1 S. H. Jin, 38 : 653-, 2000

2 G. A. Edwards, 46 : 3893-, 1998

3 L. Zhen, 36 : 1089-, 1997

4 Y. Aruga, 116 : 82-, 2016

5 A. Serizawa, 39A : 243-, 2008

6 J. H. Kim, 52 : 906-, 2011

7 L. Ding, 647 : 238-, 2015

8 Y. Birol, 391 : 175-, 2005

9 C. H. Shen, 27 : 205-, 2011

10 W. Yang, 62 : 705-, 2010

11 W. F. Miao, 40 : 873-, 1999

12 M. Z. Wang, 11 : 166-, 2002

13 Y. L. Liu, 41 : 267-, 1999

14 B. B. Straumal, 18 : 293-, 1997

15 J. S. Lee, 36 : 1355-, 1998

16 L. Zhen, 32 : 1895-, 1997

17 Y. Birol, 52 : 169-, 2005

18 Y. S. Lee, 24 : 2226-, 2014

19 J. X. Zang, 22 : 2638-, 2012

20 M. S. Kim, 51 : 1854-, 2010

21 S. Das, 32 : 4603-, 2011

22 김홍규, "쌍롤 박판주조법 및 이속압연으로 제조한 고성형성 6xxx계 Al 합금 판재" 대한금속·재료학회 50 (50): 503-509, 2012

23 고동현, "박판주조법으로 제조한 7075 알루미늄 합금판재의 기계적 특성에 미치는 소부경화처리의 영향" 대한금속·재료학회 54 (54): 483-491, 2016

24 김수현, "Grain-Structure Evolution of Brazing-Treated A4343/A3003/A4343 Aluminum Brazing Sheets Rolled with Different Reductions" 대한금속·재료학회 21 (21): 276-285, 2015

25 이광진, "Effect of Pre-Aging Conditions on Bake-Hardening Response of Al-0.4 wt%Mg-1.2 wt%Si-0.1 wt%Mn Alloy Sheets" 대한금속·재료학회 49 (49): 448-453, 2011