Ferroelectric Properties of SBT Capacitor with Annealing Times

다국어 초록 (Multilingual Abstract)

The Sr$\_$0.7/Bi$\_$2.3/Ta$_2$O$\_$9/(SBT)thin films are deposited on Pt-coated electrode (Pt/TiO$_2$/SiO$_2$/Si) using a RE magnetron sputtering method. The ferroelectric properties of SBT capacitors with annealing times were studied. As a result of conducting the X-ray diffraction analysis and the electron microscopy analysis, the perovskite phase began to grow from 10 minutes after annealing the specimen, and excellent crystallization was accomplished at 60 minutes after annealing the specimen. The remanet polarization (2P$\_$r/) value and the coercive electric field (E$\_$c/) of the SBT thin film specimen showed the most excellent characteristics at 60 minutes after annealing the specimen, which were approximately 12.40 C/$\textrm{cm}^2$ and 30 kV/cm, respectively. The leakage current density of the SBT thin film specimen as annealed for 60 minutes was approximately 2.81${\times}$10$\^$－9/A/$\textrm{cm}^2$.