The effect of Mn on cavitation erosion resistance and the sliding wear resistance of Fe-base hardfacing NewAlloy was investigated. Mn is known to decrease stacking fault energy and enhance the formation of $\varepsilon$-martensite. Cavitation erosion ...
The effect of Mn on cavitation erosion resistance and the sliding wear resistance of Fe-base hardfacing NewAlloy was investigated. Mn is known to decrease stacking fault energy and enhance the formation of $\varepsilon$-martensite. Cavitation erosion resistance for 50 hours and sliding wear resistance for 100 cycles were evaluated by weight loss. Fe-base hardfacing NewAlloy showed more excellent cavitation erosion resistance than Mn-added NewAlloys. $\Upsilon-\alpha$' phase transformation that can enhance erosion resistance by matrix hardening occurred in every specimens. But, only in Mn free Fe-base hardfacing NewAlloy, the hardened matrix could repress the propagation of cracks that was initialed at the matrix-carbides interfaces more effectively than Mn-added NewAlloy The Mn free Fe-base hardfacing NewAlloy showed better sliding wear resistance than Mn-added alloys. Mn-addition up to 5wt.% couldn't increase the sliding wear and cavitation erosion resistance of Fe-base hardfacing alloy because it didn't make $\Upsilon\to\varepsilon$ martensite phase transformation. Therefore, it is considered that the cavitation erosion and the sliding wear resistance can be improved due to $\Upsilon\to\varepsilon$ martensite phase transformation when Mn is added more than 5wt.% in Fe-base hardfacing alloys.