Field-induced Strain Memory with Non-180˚ Domain-reorientation Control

다국어 초록 (Multilingual Abstract)

Using non-180˚ domain-reorientation control, we propose the strain memory effect in ferroelectric ceramics. Electric fields with asymmetric amplitudes were applied to soft-type lead zirconate titanate (PZT) ceramics, and the strain hysteresis and the polarization loop were measured. The butterfly curve became asymmetric under an electric field with a particular asymmetric amplitude. The asymmetric butterfly curve had two stable strain states at zero electric field. Thus, the strain memory effect was realized as the difference between the two stable strain states. An XRD analysis was carried out to verify the contribution of the non-180˚ domain reorientation to the strain memory effect. The non-180˚ domain reorientation was determined as the intensity ratio of the (002) to the (200) peak. The strain memory determined from macroscopic strain measurements had a linear relationship to the non-180 domain volume fraction. This result indicated the origin of the strain memory to be the non-180˚ domain reorientation.

참고문헌 (Reference)

1 R. E. Jones, Jr., 270 : 584-, 1995

2 N. Uchida, 4 : 867-, 1965

3 E. Benes, 48 : 1-, 1995

4 K. Nakamura, 26 : 198-, 1987

5 A. Kawamata, 135 : 782-, 2007

6 T. Granzow, 87 : 212901-, 2005

7 X. Ren, 3 : 91-, 2004

8 W. Liu, 438 : 350-, 2006

9 T. Tsurumi, 36 : 5970-, 1997

10 E. C. Subbarao, 28 : 1194-, 1957

11 J. L. Jones, 97 : 034113-, 2005

12 H. Kungl, 55 : 1849-, 2007

13 A. Pramanick, 56 : 1546-, 2009

14 M. Hammer, 81 : 721-, 1998

15 H. Cao, 76 : 890-, 1993

16 N. Balke, 90 : 1088-, 2007

17 K. Uchino, 7 : 273-, 1998