Nd8Fe86-xNbxB6 (x = 0, 1, 2, 3) 초미세립복합상 영구자석의 자기적 특성 연구 = Characterization of the Intergranular Phase in a Nd8Fe86-xNbxB6 (x = 0, 1, 2, 3) Nanocomposite Magnet by Using Mössbauer Spectroscopy

다국어 초록 (Multilingual Abstract)

A precisely refined Mössbauer study revealed that the
intergranular phase that forms between the α-Fe and the
Nd2Fe14B phases in NdFeNbB alloys plays a significant role
in the magnetic properties. By the addition of Nb into the
Nd8Fe86B6 composition, the coercivity was found to be
increased by 25% due to a refinement of the average grain size of
both the soft and the hard magnetic phases, which decreased from 50
nm for virgin Nd8Fe86B6 to 25 nm for
Nd8Fe86B6 alloys. Nb addition was confirmed to
stabilize the Nd8Fe86B lattice by preventing thermal
vibration of the sites in the Nd8Fe86B lattice at which Fe
atoms were replaced by Nb atoms. The enhanced coercivity originated
the exchange hardening of the soft and amorphous phases surrounding
the hard magnetic Nd8Fe86B crystals.

국문 초록 (Abstract)

NdFeNbB 합금에서 α-Fe와 Nd2Fe14B상 사이에 형성된 입간결정립이 초미세립 복합상의 자기특성에 큰 영향을 미치고 있음을 정밀한 뫼스바우어 분광학 분석을 통해 조사하였다.
Nd2Fe14B+α-Fe 재료에서 얻은 최대자기특성은 Br = 9.791 kG, iHc = 5.565 kOe, 그리고 (BH)max = 14.61 MGOe였고, 이 경우, 각 존재상의 부피분율은 α-Fe; 24.2%, Nd2Fe14B; 53.1%, 입자간; 22.7 %였음을 확인하였다.
Nd8Fe86B6 조성에 첨가한 Nb는 평균 입자 크기를 50 nm에서
25 nm로 정제함으로써 보자력을 25% 정도 증가시켰다. 첨가원소 Nb의
역할은 Nd2Fe14B 격자의 열적진동을 억제함으로써
Nd2Fe14B 격자를 안정화시킴은 물론 연자성상 α-Fe의
교환경화를 일으킴으로 인해 보자력을 증가시켰다.

참고문헌 (Reference)

1 R. Skomski, 48 : 812-, 1993

2 T. Schrefl, 76 : 7053-, 1994

3 T. Schrefl, 81 : 5567-, 1997

4 M. Yamasaki, 44 : 1375-, 2001

5 J. O. Oti, 29 : 1265-, 1993

6 T. Kobayashi, 87 : 6579-, 2000

7 H. N. Ok, 22 : 4215-, 1980