LDH를 함유한 PTMSP 복합막의 기체투과 특성

국문 초록 (Abstract)

본 연구에서는 높은 투과도를 갖는 PTMSP에 1, 3, 5 wt% LDH 함량으로 용액 삽입법에 의하여 PTMSP/LDH 복합막을 제조하였다. 복합막의 물리화학적 특성은 FT-IR, TGA, XRD, UTM, SEM을 사용하여 조사하였고, H_2, N2, CO2 기체에 대한 투과도와 선택도 성질을 고찰하였다. PTMSP/LDH 복합막의 기체 투과도는 LDH 함량이 증가함에 따라 감소하였고, H2와 CO2의 선택도는 LDH의 함량이 5 wt%일 때 최대값을 보였다. 그리고 PTMSP와 PTMSP/LDH 복합막은 기체투과 압력이 증가함에 따라 기체의 투과도가 증가하였다. PTMSP/LDH 복합막의 기체투과도는 PTMSP 막에 비해 압력 증가에 대한 차이가 다소 작게 나타났다.

다국어 초록 (Multilingual Abstract)

In this study, PTMSP/LDH composite membranes were prepared by the solution intercalation method with 1, 3, and 5 wt% LDH contents to PTMSP. To investigate the physico-chemical characteristics of composite membranes, the analytical methods such as FT-IR, TGA, XRD, UTM, and SEM have been utilized, and the gas permeability and selectivity properties of H2, N2, and CO2 were evaluated. The permeability of the PTMSP/LDH composite membranes decreased as LDH content increased and the selectivity H2 and CO2 showed the maximum value at 5 wt% of LDH content. Permeability of PTMSP/LDH composite membrane increased as the gas permeation pressure increased. The difference of the increase in gas permeation pressure of the permeability of PTMSP/LDH composite membrane was slightly smaller than of PTMSP membrane.

참고문헌 (Reference)

1 T. Masuda, 105 : 7473-, 1983

2 I. Pinnau, "Transport of organic vapors through poly(1-trimethylsilyl-1-propyne)" 116 : 199-, 1996

3 G. Choudalakis, "The free volume in acrylic resin/laponite nanocomposite coatings" 47 : 264-, 2011

4 타파스쿨라, "Synthesis and characterization of ethylene vinyl acetate/Mg-Al layered double hydroxide nanocomposites" JOHN WILEY SONS INC 104 (104): 1845-1851, 200705

5 L. Du, "Structural characterization and thermal and mechanical properties of poly(propylene carbonate)/MgAl-LDH exfoliation nanocomposite via solution intercalation" 66 : 913-, 2006

6 Q. Hu, "Poly(amide-imide)/TiO2 nano-composite gas separation membranes: fabrication and characterization" 135 : 65-, 1997

7 F. R. Costa, "Morphology and fpathure behaviour, Morphethylene/Mg-Al layered double hydroxide (LDH) nanocomposites" 42 : 2140-, 2006

8 Y. Mizutani, "Microporous polypropylene films containing ultrafine silica particles" 72 : 1489-, 1999

9 M. Ardanuy, "Mg-Al layered double hydroxide nanoparticles evaluation of the thermal stability in polypropylene matrix" 51 : 341-, 2011

10 F. Kovanda, "Layered double hydroxides intercalated with organic anions and their application in preparation of LDH/polymer nanocomposites" 6 (6): 111-, 2009

11 M. S. Cho, "Gel polymer electrolyte nanocomposites PEGDA with Mg-Al layered double hydroxides" 50 : 331-, 2004

12 J. M. Herrera-Alonso, "Gas transport properties of polyacrylate/clay nanocomposites prepared via emulsion polymerizstion" 363 : 48-, 2010

13 T. Kuila, "Ethylene vinyl acetate/Mg-Al LDH nanocomposites by solution blending" 497 : 2009

14 이현경, "Ethylene Vinyl Acetate/Co-Al Layered Double Hydroxide 나노복합막의 기체 투과 성질" 한국막학회 20 (20): 290-296, 2010

15 T. C. Merkel, "Effect of nanoparticles on gas sorption and transport in poly(1-trimethylsilyl- 1-propyne)" 36 : 6844-, 2003

16 S. O’Leary, "Delamination of layered double hydroxides in polar monomers: new LDH-acrylate nanocomposites" 14 : 1506-, 2002