Dielectric properties of $Ba_{0.9}Ca_{0.1}(Ti_{1-x}Sn_x)O_3$ were investigated from x=0 to 0.20, and temperature range -4$0^{\circ}C$~13$0^{\circ}C$ Density and grain size decreased with increasing Sn content due to grain growth inhibitor. Dielectric...
Dielectric properties of $Ba_{0.9}Ca_{0.1}(Ti_{1-x}Sn_x)O_3$ were investigated from x=0 to 0.20, and temperature range -4$0^{\circ}C$~13$0^{\circ}C$ Density and grain size decreased with increasing Sn content due to grain growth inhibitor. Dielectric constant below the Curie temperature increased with increasing Sn content and dissipation factor dec reased. These results are due to grain size effect and internal stress. Curie temperature was shifted to lower temperature with increasing ratio of total polarizability to volume resulting from substitution of $Ba^{2+}$ ion with $Ca^{2+}$ ion $Ti^{4+}$ ion with $Sn^{4+}$ ion.