Nd:YAG 결정과 구리 냉각 마운트 사이의 열 접촉 전도도 분석 = Analysis of the Conductivity of the Thermal Contact between a Nd:YAG Crystal and a Copper Cooling Mount

다국어 초록 (Multilingual Abstract)

The properties of the thermal contact between the laser crystal and the copper cooling mount were measured while varying the pressure applied to the surface of the laser rod and the material for heat transfer. The diameter of the Nd:YAG crystal was 3 mm and its length was 75 mm. Circulating cooling water and a thermo-electric cooler maintained the copper mount at a constant temperature. The conductance of the thermal contact was measured when a graphite sheet, a thermal conductive paste, or an indium foil was used as a heat transfer material, as well as when no heat transfer material was used. Of the materials used in the experiments, the thermal conductive paste showed the highest thermal contact conductivity. When no heat transfer material was used, the thermal-contact's conductivity increased in proportion to the pressure applied on the laser rod.

국문 초록 (Abstract)

열전달을 위한 물질과 레이저봉 표면에 가하는 압력을 달리하면서 레이저 결정과 구리 냉각 마운트 사이의 열 접촉 전도도 특성을 측정하였다. 레이저 결정의 직경은 3 mm, 길이는 75 mm이다. 냉각 마운트는 냉각수 순환과 열전 냉각기를 사용하여 일정한 온도를 유지한다. 열전달 물질을 사용하지 않은 경우를 비롯하여 열전달 물질로 흑연 시트, 열전도 페이스트 (thermal paste), 인듐 포일 등을 사용한 경우에 대하여 열 접촉 전도도를 측정하였다. 실험에 사용한 물질 중에서 열전도 페이스트가 가장 높은 열 접촉 전도도를 보였다. 열전달 물질이 없는 경우 열 접촉 전도도는 레이저봉에 가하는 압력에 비례하여 증가하였다.

참고문헌 (Reference)

1 J. Shin, 25 : 19309-, 2017

2 V. Singhal, 48 : 5446-, 2005

3 M. G. Cooper, 12 : 279-, 1969

4 E. G. Wolff, 41 : 3469-, 1998

5 J. Mendiguren, 99 : 813-, 2016

6 Y. F. Chen, 35 : 234-, 1999

7 J. Shin, 380 : 446-, 2016

8 Y. Sato, 14 (14): 10528-, 2006

9 M. K. Reed, 13 : 204-, 1988

10 J. Didierjean, 5707 : 370-, 2005

11 R. Yasuhara, 20 : 29531-, 2012

12 J. Didierjean, 16 : 8995-, 2008

13 M. Rosochowska, 135 : 204-, 2003

14 I. Kuznetsov, 4 : 2204-, 2014

15 김태성, "나노초 열반사율 시스템을 이용한 V2O5 박막의 열확산도 측정" 한국물리학회 65 (65): 644-650, 2015

16 W. Koechner, "Solid-State Laser Engineering, 5th ed." Springer Science 312-418, 1999

17 Suyong Kwon, "Reliability of Thermal Conductivity Measurement of Liquids by Using Transient Hot-Wire, Photon-Correlation Spectroscopy and the Laser Flash Method" 한국물리학회 68 (68): 1145-1155, 2016

18 L. J. Salerno, "NASA Technical Memorandum, 110429" 1997