착색액 침지 횟수와 최종 소결 온도가 지르코니아 세라믹의 굴곡강도에 미치는 영향

다국어 초록 (Multilingual Abstract)

The purpose of this study is to investigate the effect of number of times dipped in coloring liquid and sintering temperature on the flexural strength of zirconia ceramic. In this study, using a zirconia block having improved transparency, specimens with size of 25 mm × 2 mm × 1.5 mm were fabricated. The zirconia ceramic specimens were divided into three groups according to the number of times dipped in coloring liquid by 0, 2 and 4 times, and dyed in the coloring liquid to give color to each specimen. Then, after sintering them at the final temperature of 1,450°C and 1,600°C, f lexural strength was measured using a universal testing machine (total 6 group, n=10 for each group). Also, a scanning electron microscopy (SEM) was performed to observe its microstructure, and the data obtained through the experiment were analyzed with two-way ANOVA. The results of the flexural strength analysis show that the highest value was measured 762.3±42.3 MPa in EKL2 group, while the lowest value was 516.4±77.1 MPa in EKH4 group. According to the results of the two-way ANOVAs, flexural strength was not related with interaction between sintering temperature and number of times dipped in coloring liquid (R<SUP>2</SUP>=0.737). However, there were statistically significant differences in flexural strength depending on sintering temperature (P<0.001). The flexural strength of zirconia ceramics having improved transparency was dependent on sintering temperature. The number of times dipped in the coloring liquid did not affect flexural strength of the zirconia ceramic having improved transparency.

참고문헌 (Reference)

1 Piconi C, "Zirconia as a ceramic biomaterial" 20 : 1-25, 1999

2 Stawarczyk B, "The effect of zirconia sintering temperature on flexural strength, grain size, and contrast ratio" 17 : 269-274, 2013

3 Ekren Orhun, "The effect of coloring liquid dipping time on the fracture load and color of zirconia ceramics" 대한치과보철학회 9 (9): 67-73, 2017

4 Kern F, "Mechanical properties and low temperature degradation resistance of 2.5 Y-TZP–alumina composites" 65 : 258-266, 2013

5 Ban S, "Influence of test method on failure stress of brittle dental materials" 69 : 1791-1799, 1990

6 Albakry M, "Fracture toughness and hardness evaluation of three pressable all-ceramic dental materials" 31 : 181-188, 2003

7 Aboushelib MN, "Effect of zirconia type on its bond strength with different veneer ceramics" 17 : 401-408, 2008

8 Hjerppe J, "Effect of shading the zirconia framework on biaxial strength and surface microhardness" 66 : 262-267, 2008

9 Pecho OE, "Color and translucency of zirconia ceramics, human dentine and bovine dentine" 40 : 34-40, 2012

10 Al‐Amleh B, "Clinical trials in zirconia: a systematic review" 37 : 641-652, 2010

11 Sreeram KJ, "Cerium molybdenum oxides for environmentally benign pigments" 75 : 687-692, 2007

12 Tekeli S, "A quantitative assessment of cavities in 3 mol% yttria-stabilized tetragonal zirconia specimens containing various grain size" 28 : 785-789, 2002