The presence of chloride (Cl-) ions in environments causes localized corrosion resulting decrease the durability of the structures. In this study, 5% Mg containing Al alloys (Al-5Mg) wire used vis-à-vis compared its corrosion resistance with pure Al ...
The presence of chloride (Cl-) ions in environments causes localized corrosion resulting decrease the durability of the structures. In this study, 5% Mg containing Al alloys (Al-5Mg) wire used vis-à-vis compared its corrosion resistance with pure Al in 3.5wt.% NaCl solution with exposure periods. Initially both wires exhibited identical open circuit potential (OCP) attributed to the presence of native oxide film on the surface but with the exposure periods it shifted towards active direction owing to the dissolution of oxide film. The pure Al continuously shifted the OCP towards active direction while Al-5Mg shows stabilization of OCP after 8 days of exposure. The OCP of Al-5Mg is slightly higher compared to pure Al wire owing to the activeness of Mg. The total impedance of the Al-5Mg alloy is almost three times greater than pure Al with exposure periods in 3.5 wt.% NaCl solution. It might be formation of Al-Mg LDH (layered double hydroxide) thin film onto the surface.