폐병유리의 다공질 재료화

다국어 초록 (Multilingual Abstract)

Porous materials were manufactured by hydrothermal treatment of waste bottle glass without foam agent. The optimal condition for the hydrolysis was found with 45㎛ particle size of raw material, 20wt% distilled water, 200℃ reaction temperature and 6hr reaction time by using experimental design. Under this condition, the porosity, compressive strength, and thermal conductivity of porous materials were identified as 81.1~89.2%, 74.71±1.11~25.44±2.34kgf/cm² and 0.0309±0.0030~0.04395±0.0031kcal/Hm℃, respectively. The result of these numerical values were comparing with those of ALC (autoclaved lightweight concrete), although it has higher porosity than for ALC.

목차 (Table of Contents)

• Ⅰ. 서론 = 1
• Ⅱ. 이론적 배경 = 3
• 1. 소다석회 유리의 가수분해 반응 = 3
• 2. 실험계획법(design of experiments) = 4
• 1) 실험계획법이란? = 4
• 2) 실험계획법의 순서 = 5
• 3) 실험계획의 기본원리 = 6
• 4) 구조모형 = 7
• 5) 요인배치법 = 8
• 6) 분산분석이란 = 9
• Ⅲ. 실험 방법 = 10
• 1. 수열반응 조건 선정 = 10
• 2. 수열반응에 투입되는 폐유리 입자 size의 영향 = 12
• 3. 소결 온도에 따른 영향 = 12
• 4. 폐병유리를 이용한 다공질 재료의 제조 방법 = 14
• 5. 분석 방법 = 14
• Ⅳ. 결과 및 고찰 = 19
• 1. 수열합성 한 폐병유리 분말 = 19
• 2. 수열반응 온도와 증류수량 = 24
• 3. 원료의 입자 size 영향 = 30
• 4. 소결 온도에 따른 영향 = 36
• Ⅴ. 결론 = 46