전력케이블에서 반도전 재료(층)의 불순물 측정 및 물성에 관한 연구 = A Study on Impurities Measurement and Physical Properties of Semiconductive Shield at Power Cable

다국어 초록 (Multilingual Abstract)

In this paper, we investigated impurities content and physical properties showing by changing the content of carbon black that is semiconductive materials for underground power transmission. Specimens were made of sheet form with the three of existing resins and the nine of specimens for measurement. Impurities content of specimens was measured by ICP-AES (Inductively Coupled Plasma Atomic Emission Spectrometer), and density of specimens were measured by density meter. And then specific heat (Cp) was measured by DSC (Differential Scanning Calorimetry). A ranges of measurement temperature were from 0[℃] to 200[℃], and heating temperature was 4[℃/min]. Impurities content was highly measured according to increasing the content of carbon black from this experimental result, also density was increased according to these properties. Especially impurities content values of the A1 and A2 of existing resins were measured more than 4000[ppm]. Specific heat from the DSC results was decreased according to increasing the content of carbon black. Because ionic impurities of carbon black having Fe, Co, Mn, Al and Zn are rapidly passed kinetic energy increasing the number of times breaking during the unit time with the near particles according to increasing vibration of particles by the applied heat energy.

참고문헌 (Reference)

1 박수진, "충전재-탄성체 상호작용. 6. 산소 플라즈마 처리가 카본블랙 표면특성에 미치는 영향" 37 (37): 99-106, 2002.

2 한재홍, "에틸렌 비닐 아세테이트 공중합체/에틸렌 아크릴산 공중합체 블렌드의 이온투과 및 물리적 성질" 45 (45): 1996.

3 한재홍, "반도전층내 불순물이 전력케이블의 신뢰도에 미치는 영향" 46 (46): 1997.

4 M. T. Shaw, "Water Treeing in Solid Dieletrics" 19 : 419-452, 1993.

5 M. J. Given, "The Role of Ions in the Mechanism of Water Tree Growth" 22 : 151-156, 1987.

6 전용구, "EVA의 Vinyl Acetate 함량변화에 따른 열적-기계적 성질 연구" 15 (15): 402-410, 1991.

7 한전 표준 구매시방서, "22.9kV 동심중성선 전력케이블＂"