The purpose of this laboratory study was to evaluate the fatigue resistance, fracture resistance and mode of failure of posterior hybrid‐abutment‐crown vs. hybrid‐abutment with separate crown, both bonded to short titanium bases. Thirty‐two ti...
http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
https://www.riss.kr/link?id=O118947710
2019년
-
0905-7161
1600-0501
SCI;SCIE;SCOPUS
학술저널
90-98 [※수록면이 p5 이하이면, Review, Columns, Editor's Note, Abstract 등일 경우가 있습니다.]
0
상세조회0
다운로드다국어 초록 (Multilingual Abstract)
The purpose of this laboratory study was to evaluate the fatigue resistance, fracture resistance and mode of failure of posterior hybrid‐abutment‐crown vs. hybrid‐abutment with separate crown, both bonded to short titanium bases. Thirty‐two ti...
The purpose of this laboratory study was to evaluate the fatigue resistance, fracture resistance and mode of failure of posterior hybrid‐abutment‐crown vs. hybrid‐abutment with separate crown, both bonded to short titanium bases.
Thirty‐two titanium implants were embedded perpendicularly in auto‐polymerizing resin. Implant‐supported restorations simulating a maxillary first premolar were designed and milled using a CAD/CAM system and divided into 2 groups according to material (n = 16): zirconia (Z) and lithium disilicate (L). Each group was subdivided into two subgroups according to design (n = 8): hybrid‐abutment‐crown (ZS, LS) and hybrid‐abutment with separate crown (ZC, LC). Each group was subjected to 1.2 million cycles of thermo‐mechanical fatigue loading in a dual‐axis chewing simulator at 120 N load. Surviving specimens were subjected to quasi‐static loading in a universal testing machine. Mode of failure was determined under a low magnification optical microscope.
During chewing simulation, 18.8% of zirconia and 43.8% of lithium disilicate restorations failed. The fracture resistance median values ranged from 3,730 N for group ZC, 3,400 N for group ZS, 1,295 N for group LS to 849 N for group LC. Group ZC had a statistically significant higher fracture resistance than groups LC and LS; however, it did not differ significantly from group ZS (p ≤ 0.05). Failures were seen in both titanium bases and ceramic superstructure.
Zirconia and lithium disilicate hybrid implant‐supported restorations with short (3 mm) titanium bases failed in a considerable number already during chewing simulation. Therefore, despite their high fracture strength the use in the posterior region should be considered critically.