The oxygen flux of SDC ($Sm_2O_3\;doped\;CeO_2$) solid electrolyte membranes with electronic and oxygen ion-ic conductivities has been investigated as a basic research in order to develop the conversion process of na-tural gas to syngas using the cera...
The oxygen flux of SDC ($Sm_2O_3\;doped\;CeO_2$) solid electrolyte membranes with electronic and oxygen ion-ic conductivities has been investigated as a basic research in order to develop the conversion process of na-tural gas to syngas using the ceramic membrane reactor. Tube type membranes(1 mm thickness) were fa-bricated by slip casting of SDC powders prepared by the oxalate coprecipitaion method. Dense oxygen per-meation membranes(0.1 mm thickness) could be synthesized via sintering at $1450^{\circ}C$ for 2h and their re-lative density was over 95% The oxygen flux through SDC membranes doped 20mol% $Sm_15$ was about $1.13{\times}10^{-5}\;mol/m_2{\cdot}sec$ at low temperature around $800^{\circ}C$. In addition the SDC membranes showed a good thermaal stability for a long period of service.