자외선을 처리한 목재 플라스틱 복합재의 물리 및 역학적 성질 평가 = Evaluation on Physical and Mechanical Properties of Wood Plastic Composites Treated under Ultraviolet Irradiation

다국어 초록 (Multilingual Abstract)

In this study, we received each wood plastic composites (WPC) from three manufacturers. These WPCs were evaluated regarding their physical and mechanical properties of both before and after accelerated weathering by ultraviolet (UV) irradiation. The total time of exposure of the WPCs to UV irradiation was 1800 h. The water absorption, volumetric swelling and shrinkage of WPCs did not affected by UV irradiation. Among the mechanical properties, there was no significant differences in bending strength and screw withdrawal resistance of UV treated WPCs compared with those of reference WPCs. However, surface hardness of WPCs showed decrease under UV irradiation. Stereoscopic microscopy observation revealed deterioration of the surface layer polymer in all weathered WPCs by UV. Exposure of the WPCs to UV irradiation caused decomposition and disappearance of the polymer layer. From this result, we can estimate that damage of polymer by UV led to a decrease in the surface hardness of the WPCs. The wood flours retained original shape after accelerated weathering by UV irradiation.

참고문헌 (Reference)

1 전상진, "폴리인산염 첨가에 의한 폴리프로필렌 기반의 Wood Plastic Composites 열안정성" 한국목재공학회 42 (42): 682-690, 2014

2 김철현, "폐지 복합재료의 물성" 한국펄프·종이공학회 40 (40): 48-52, 2008

3 김범준, "유리섬유가 충전된 공압출 목재⋅플라스틱 복합재의 굽힘 특성에 관한 연구" 한국가구학회 24 (24): 379-388, 2013

4 강인애, "목분-폴리프로필렌 복합재의 수분흡수율 : 목재수종, 충진제 입자크기 및 상용화제의 영향" 한국목재공학회 38 (38): 298-305, 2010

5 강인애, "목분-폴리프로필렌 복합재의 기계적 특성: 목재수종, 충진제 입자크기 및 상용화제의 영향" 한국목재공학회 37 (37): 505-516, 2009

6 신백우, "목분-고밀도폴리에틸렌 복합체의 연소성 및 열적특성" 한국화재소방학회 26 (26): 89-95, 2012

7 이세나, "대나무 분말의 함량 및 입자크기에 따른 바이오복합재의 물성 평가" 한국목재공학회 37 (37): 310-319, 2009

8 Fabiyi James S., "Wood plastic composites weathering : Visual appearance and chemical changes" 93 (93): 1405-1414, 2008

9 Lei Yong, "Wood plastic composites based on microfibrillar blends of high density polyethylene/poly(ethylene terephthalate)" 101 (101): 3665-3671, 2010

10 Benthien Jan T., "Thickness swelling and water absorption of WPC after immersion in cold anc boiling water" 71 : 437-442, 2013

11 Liu Yang, "Study on the surface properties of wood/polyethylene composites treated under plasma" 257 (257): 1112-1118, 2010

12 Islam M. N., "Study of water absorption behavior in wood plastic composites by using neutron radiography techniques" 42 (42): 925-934, 2003

13 Wechsler Andrea, "Some of the properties of wood-plastic composites" 12 (12): 2637-2644, 2007

14 Kamdem D. Pascal, "Properties of wood plastic composites made of recycled HDPE and wood flour from CCA-treated wood removed from service" 36 (36): 347-355, 2004

15 Ayrilmis Nadir, "Potential use of decayed wood in production of wood plastic composite" 74 (74): 279-284, 2015

16 H’ng Pak San, "Physical and bending properties of injection moulded wood plastic composites boards" 3 (3): 13-19, 2008

17 Mankowski Mark, "Patterns of fungal attack in wood-plastic compisites following exposure in a soil block test" 32 (32): 340-345, 2000

18 Azuma Y., "Outdoor and accelerated weathering tests for polypropylene and polypropylene/talc composites : A comparative study of their weathering behavior" 94 (94): 2267-2274, 2009

19 Gozdecki C., "Mechanical properties of woodpolymer composites with different polymers" 74 : 82-85, 2011

20 Naumann Annette, "Material resistance of weathered wood-plastic composites against fungal decay" 75 : 28-35, 2012

21 Stark Nicole M., "Influence of photostabilizers on wood flour-HDPE composites exposed to xenon-arc radiation with and without water spray" 91 (91): 3048-3056, 2006

22 Lomeli-Ramirez M. G., "Evaluation of accelerated decay of wood plastic composites by Xylophagus fungi" 63 (63): 1030-1035, 2009

23 Li Rongzhi, "Environmental degradation of wood-HDPE composite" 70 (70): 135-145, 2000

24 Lee Chia-Huang, "Effects of polymeric matrix on accelerated UV weathering properties of wood-plastic composites" 66 : 981-987, 2012

25 Gwon Jae Gyoung, "Effects of chemical treatments of hybrid fillers on the physical and thermal properties of wood plastic composites" 41 : 1491-1497, 2010

26 Kim Tae-Woo, "Effect of silane coupling on the fundamental properties of wood flour reinforced polypropylene composites" 45 (45): 1595-1605, 2010

27 Bengtsson Magnus, "Durability and mechanical properties of silane cross-linked wood thermoplastic composites" 67 (67): 2728-2738, 2007

28 Adihikary Kamal B., "Dimensional stability and mechanical behaviour of wood-plastic composites based on recycled and virgin high-density polyethylene(HDPE)" 39 (39): 807-815, 2008

29 Yang Te-Hsin, "Characterization of the property changes of extruded wood-plastic composits during yeat roung subtropical weathering" 88 (88): 159-168, 2015

30 Ashori Alireza, "Characteristics of wood-fiber plastic composites made of recycled materials" 29 (29): 1291-1295, 2009

31 Butylina Svetiana, "Accelerated weathering of wood-polypropylene composites containing minerals" 43 (43): 2087-2094, 2012

32 La Mantia F. P., "Accelerated weathering of polypropylene/wood flour composites" 33 (33): 1252-1258, 2008