<P>High temperature oxidation behavior of Si-Mo ferritic ductile cast iron was investigated in the point of the effect of chromium and vanadium addition. The addition of Cr promoted the formation of as-cast pearlite around carbide which exists i...
http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
https://www.riss.kr/link?id=A107589795
2010
-
SCOPUS
학술저널
542-545(4쪽)
0
상세조회0
다운로드다국어 초록 (Multilingual Abstract)
<P>High temperature oxidation behavior of Si-Mo ferritic ductile cast iron was investigated in the point of the effect of chromium and vanadium addition. The addition of Cr promoted the formation of as-cast pearlite around carbide which exists i...
<P>High temperature oxidation behavior of Si-Mo ferritic ductile cast iron was investigated in the point of the effect of chromium and vanadium addition. The addition of Cr promoted the formation of as-cast pearlite around carbide which exists in cell boundary, which was eliminated during annealing process. The addition of vanadium promoted the precipitation of tiny carbide and reduced the grain size of ferrite. As the test temperature increased, the change of volume increased, on the other hand, the change of weight decreased above 1173K. In the case of Cr added specimen, the change of weight decreased with the increase of test temperature because of the presence of Cr oxide layer. The vanadium added specimens showed higher increase in the weight and volume change. The oxide layer of vanadium added specimen had very porous structure and showed severe internal oxidation. It is due to the catastrophic oxidation characteristic of vanadium alloyed ferrous alloy. </P>
Electromagnetic Continuous Casting Process for Near Net Shape Aluminum Alloy Billet
New SMA Actuator with High Energy Efficiency and Quick Response