은이 코팅된 Copper(I) Oxide 나노 입자 및 도전성 페이스트의 제조 특성 = Fabrication and Characterization of Silver Copper(I) Oxide Nanoparticles for a Conductive Paste

다국어 초록 (Multilingual Abstract)

This study investigates Ag coated $Cu_2O$ nanoparticles that are produced with a changing molar ratio of Ag and $Cu_2O$. The results of XRD analysis reveal that each nanoparticle has a diffraction pattern peculiar to Ag and $Cu_2O$ determination, and SEM image analysis confirms that Ag is partially coated on the surface of $Cu_2O$ nanoparticles. The conductive paste with Ag coated $Cu_2O$ nanoparticles approaches the specific resistance of $6.4{\Omega}{\cdot}cm$ for silver paste(SP) as $(Ag)/(Cu_2O)$ the molar ratio increases. The paste(containing 70 % content and average a 100 nm particle size for the silver nanoparticles) for commercial use for mounting with a fine line width of $100{\mu}m$ or less has a surface resistance of 5 to $20{\mu}{\Omega}{\cdot}cm$, while in this research an Ag coated $Cu_2O$ paste has a larger surface resistance, which is disadvantageous. Its performance deteriorates as a material required for application of a fine line width electrode for a touch panel. A touch panel module that utilizes a nano imprinting technique of $10{\mu}m$ or less is expected to be used as an electrode material for electric and electronic parts where large precision(mounting with fine line width) is not required.

참고문헌 (Reference)

1 H. S. Lee, 12 : 23-, 2009

2 D. A. Roberson, 4 : 963-, 2011

3 W. Su, 172 : 716-, 2009

4 L. Mai, 257 : 974-, 2010

5 L. Pan, 6 : 1019-, 2011

6 A. Alistan-Grijalva, 25 : 438-, 2005

7 Minghua Li, 45 : 8989-, 2011

8 J. H. Jin, 19 : 96-, 2009

9 S. K. Gandomani, 40 : 7957-, 2014

10 S. Gayathri, 1 : 8-, 2015

11 X. Yang, 9 : 1607-, 2008

12 H. Zhang, 43 : 2905-, 2009

13 H. E. Chao, 23 : 1457-, 2003

14 O. Akhavan, 336 : 117-, 2009

15 U. G. Akpan, 375 : 1-, 2010

16 H. Xiaomiao, 257 : 4935-, 2011

17 Y. Yonezawa, 171 : 1-, 2005

18 M. Meyer, 2 : 90-, 1984

19 M. Boutonnet, 5 : 209-, 1982

20 F. Ghanbary, 5 : 2889-, 2011

21 Lizhi Zhang, 6 : 684-, 2005

22 Yong-Jin Kim, "Synthesis of gold-coated iron nanoparticles by a reverse micelle method" 세라믹연구소 10 (10): 216-218, 2009

23 N. Y. Jamil, "Preparation, Structural and Optical Characterization of ZnO/Ag Thin Film by CVD" 3 : 3-, 2014

24 C. F. Bohren, "John Wiley & Sons, Inc."

25 박혜림, "Aging 효과에 따른 나노메탈(Au, Ag)-이산화티탄 복합체의 항균 활성도" 한국공업화학회 23 (23): 293-296, 2012