Effects of Strontium Gallate Addition on Sintering Behavior and Electrical Conductivity of Yttria-Doped Ceria

다국어 초록 (Multilingual Abstract)

The densification behavior and electrical conductivity of Ce0.8Y0.2O1.9 ceramics with strontium gallate concentrations ranging from 0 to 5 mol. % were investigated. The sintered density was found to increase rapidly for concentrations up to 0.5 mol. % Sr2Ga2O5 and then to decrease upon further Sr2Ga2O5 addition. It was possible to obtain dense Ce0.8Y0.2O1.9 ceramics with 95% of the theoretical density using a 0.5 mol. % Sr2Ga2O5- added specimen sintered at 1250°C for 5 h, whereas pure Ce0.8Y0.2O1.9 ceramics needed to be sintered at 1550°C in order to obtain an equivalent theoretical density. The electrical conductivity was measured as a function of the dopant content over the temperature range of 450°C - 700°C in air. The conductivity of the 0.5 mol. % Sr2Ga2O5-added specimen showed a maximum value of 4.43 × 10−3 Ω−1·cm−1 at 700°C. The addition of Sr2Ga2O5 was found to promote the sintering properties and electrical conductivities of Y2O3-doped CeO2.

참고문헌 (Reference)

1 H. Inaba, 83 : 1-, 1996

2 K. Eguchi, 52 : 165-, 1992

3 A. Overs, 65 : 606-, 1982

4 P. L. Chen, 76 : 1577-, 1993

5 Y. C. Zhou, 8 : 1689-, 1993

6 K. Yamashita, 81 : 53-, 1995

7 A. K. Bhattacharya, 31 : 5005-, 1996

8 J. V. Herle, 86-88 : 1255-, 1996

9 K. Higashi, 14 : 957-, 1996

10 H. Yoshida, 82 : 219-, 1999

11 J. S. Lee, 39 : 2025-, 2004

12 J. V. Herle, 80 : 933-, 1997

13 J. S. Lee, 30 : 807-, 2004

14 K. H. Choi, 463 : 484-, 2008

15 T. Zhang, B83 : 235-, 2001

16 T. Zhang, 21 : 2221-, 2001

17 C. M. Kleinlogel, 135 : 567-, 2000

18 C. M. Kleinlogel, 5 : 231-, 2000

19 J. S. Lee, 17 : 709-, 2006

20 J. S. Lee, 474 : 219-, 2009

21 L. Gao, 195 : 3130-, 2010

22 V. P. Kobzareva, 21 : 903-, 1976

23 M. Feng, 77 : 1954-, 1994

24 Hui-Eun Kim, "Electrical properties of Ga_2O_3-added Ce_(0.8)Gd_(0.2)O_(1.9) ceramics prepared by commercial powders" 대한금속·재료학회 7 (7): 319-322, 2011