Effects of residual white rust of inorganic zinc silicate primer on corrosion protection of epoxy-coated carbon steel

다국어 초록 (Multilingual Abstract)

Inorganic zinc silicate primer is widely used in shipbuilding as a preconstruction primer (or shop primer)on steel plates; however, white rust of zinc is formed on inorganic-zinc-silicate-coated steel surfaces exposed to outdoor conditions such as rain and humidity. In this study, effects of residual white rust of inorganic zinc silicate primer on corrosion protection of epoxy-coated carbon steel were examined by water ballast simulation and condensation chamber tests. Pull-off adhesion, blistering, and cathodic disbondment tests were also performed for the same purpose. Test results clearly indicated that the residual white rust did not affect the corrosion protection when the steel surface was treated with light to heavy sweep blasting.
2010 The Korean Society of Industrial and Engineering Chemistry. Published by Elsevier B.V. All rights reserved.

참고문헌 (Reference)

1 E.L. Koehler, 40 : 5-, 1984

2 S. Feliu, 61 : 63-, 1989

3 A.G. Smith, 17 : 42-, 1978

4 H. Leidheiser, 32 : 69-, 1976

5 R.R. Wiggle, 40 : 174-, 1968

6 L. Sziraki, 46 : 3743-, 2001

7 C.E. Bird, 16 : 14-, 1977

8 T.K. Ross, 40 : 186-, 1983

9 J.E.O. Mayne, 22 : 109-, 1944

10 J.E.O. Mayne, 66 : 93-, 1947

11 O.O. Knudsen, 54 : 224-, 2005

12 T.K. Ross, 40 : 186-, 1963

13 D.S. Newton, 48 : 382-, 1965

14 F. Theiler, 14 : 405-, 1974

15 T.K. Ross, 17 : 341-, 1977

16 T. Szauer, 67 : 13-, 1984

17 S.A. Lndovist, 68 : 10-, 1985

18 E.L. Koehler, 33 : 209-, 1977

19 S. Feliu, 61 : 71-, 1989

20 J.V. Ritter, 54 : 51-, 1982

21 K. Videm, "The Electrochemical behavior of Steel in Concrete and How to Evaluate the Corrosion Rate" 96 : 348-, 1996

22 "Pull-off test for adhesion"

23 Annex 1, "Performance standard for protective coatings for dedicated seawater water ballast tanks in all types of ships and double side skin spaces of bulk carriers"

24 "Paints and varnishes – Evaluation of degradation of coatings – Designation of quantity and size of defects, and of intensity of uniform changes in appearance – Part 2 & Part 3"

25 "Paints and varnishes – Determination of resistance to humidity – Part 1. Continuous condensation"

26 R.J. Brodd, "Encyclopedia of Electrochemistry of the Elements, vol. 6" Marcel Decker 35-, 1976

27 X.G. Zhang, "Corrosion and Electrochemistry of Zinc" PlenumPress 241-, 1996

28 C.G. Munger, "Corrosion Prevention by Protective Coatings, 2nd ed" NACE 1999

29 A. Forsgren, "Corrosion Control Through Organic Coatings" CRC Press 106-, 1996

30 Recommended Practice, "Cathodic Protection Design"