금운모계 결정화유리에 관한 연구 = A Study on the Glass-Ceramics of the Eluorphlogopite System

다국어 초록 (Multilingual Abstract)

Glasses in K2O-Na2O-MgO-Al2O3-SiO2-F system were crystallized to prepare machinable glass-ceramics. The optimum nucleating and crystal growing temperatures were approximately $700^{\circ}C$ and 1060~112$0^{\circ}C$, respectively for the samples investigated. Crystalline phases of sellaite, norbergite, and fluorphlogopite appeared progressively as heat-treatment temperature was increased. Surface roughness of the crystallized specimens after the machining was similar to that of metal aluminum (2.18 ${\mu}{\textrm}{m}$). Thermal expansion coefficient, Vickers hardness and dielectric constants of the fluorphlogopite glass-ceramics prepared were 7.37~10.21 ($\times$10-6/$^{\circ}C$), 302~456kgf/$\textrm{mm}^2$ and 5.97~16 respectively.