The Ba1-xSrxTiO3 thin films deposited on ITO-coated glass substrate at 55$0^{\circ}C$ by rf magnetron sputtering method have individual preferential orientations as a function of composition (X=0, 0.25, 0.5, 0.75, 1) due to the stress relief interacti...
The Ba1-xSrxTiO3 thin films deposited on ITO-coated glass substrate at 55$0^{\circ}C$ by rf magnetron sputtering method have individual preferential orientations as a function of composition (X=0, 0.25, 0.5, 0.75, 1) due to the stress relief interactions among the intrinsic compressive stress, thermal tensile stress adn extrinsic compressive stress (compressive stress in case of BaTiO3(Tc=12$0^{\circ}C$) and Ba0.75Sr0.25TiO3(Tc=57$^{\circ}C$)). This behavior also appears on the (BaSr)TiO3 thin films (X=0.5) deposited on ITO-coated glass substrate at deposition temperature between 35$0^{\circ}C$ and 55$0^{\circ}C$. The composition of Ba1-xSrxTiO3 thin films deposited on ITO-coated glass substrate at 55$0^{\circ}C$ is close to stoichiometry (1.009~1.089 in A/B ratio), but the compositional deviation from a stoichiometry is larger as SrTiO3 is added. The morphology of Ba1-xSrxTiO3 thin films is very similar for over all substrate temperatures, and the roughness due to the differences of cluster size is the smallest at X=0.25.