Reduced Pressure Curing on Polycarbosilane Precursor for Synthesis of Silicon Carbide Fiber

다국어 초록 (Multilingual Abstract)

Low pressure curing method with iodine vapor was used on low softening temperature polycarbosilane (PCS) precursor for fabrication of continuous SiC fiber at relatively low temperature. The low curing temperature can provide with a wide range of softening temperature PCS precursors, especially with low softening PCSs, which have a good spinnability, but many difficulties with conventional oxidation curing method. The low pressure curing method having the presence of iodine vapor have shown the more positive effect on pyrolysis with early stage crystallization of β-SiC at 1300 ℃. Crystal size of β-SiC, cured at 0.008 kPa is around 2-3 nm larger than cured at 101 kPa. In addition, the higher tensile strength of SiC fiber at elevated temperature can be obtained at 0.008 kPa with a value of 2.1 GPa, compare to 1.3 GPa at 101 kPa of curing pressure condition.

참고문헌 (Reference)

1 A. R. Bunsell, 41 : 823-, 2006

2 K. E. Kim, 6 : 59-, 2017

3 P. Colombo, 93 : 1805-, 2010

4 H. J. Hwang, 134 : 13-, 2012

5 Y. Hasegawa, 51 : 161-, 1994

6 W. Toreki, 51 : 145-, 1994

7 M. D. Sacks, 19 : 2305-, 1999

8 A. Otsuka, 23 : 3125-, 2003

9 M. Takeda, 258-263 : 1594-, 1998

10 Z. Su, 98 : 2014-, 2015

11 H. Li, 44 : 970-, 2009

12 W. Li, 41 : 7011-, 2006

13 Y. Hasegawa, 2 : 161-, 1992

14 Z. Xie, 42 : 10439-, 2016

15 Z. Su, 93 : 679-, 2010

16 J. Hong, 2 : 2781-, 2014

17 Hong, 132 : 42687-, 2015

18 J. Hong, 5 : 83847-, 2015

19 R. K. Gupta, 3 : 27-, 2011

20 H. Q. Ly, 36 : 4037-, 2001

21 Y. Hasegawa, 15 : 720-, 1980

22 H. Q. Ly, 36 : 4045-, 2001

23 J. J. Sha, 57 : 6-, 2006

24 J. J. Sha, 329-333 : 592-, 2004

25 R. Q. Yao, 31 : 777-, 2008

26 김동표, "The Kinetics of Oxidation Curing of Polycarbosilane Fibers" 한국화학공학회 21 (21): 901-904, 2004