글레이즈 처리한 다색 리튬 디실리케이트와 지르코니아의 색조비교

다국어 초록 (Multilingual Abstract)

The purpose of this study was to investigate the effect of glazing treatment of multi-colored zirconia disc and lithium disilicate block on the optical properties. From an Ultra Translucent Multi-Layered (UTML) disc containing 50% cubic crystal and a lithium disilicate-based Amber Mill Direct (AMD) block, the 1.2 mm thick specimens of the upper layer (T), the center (M), and the lower layer (B) were prepared. Three types of paste glaze of InSync Glaze Paste, IPS E.max Ceram Glaze Paste, and Amber Ceram G7 Glaze Paste were applied and fired to a uniform thickness on the surface of the specimen. CIE L<SUP>*</SUP>, a<SUP>*</SUP>, b<SUP>*</SUP> values were measured using a spectrophotometer and contrast and translucency were calculated. The bonding interface with the glaze layer was observed using HR FE-SEM. In the glazed groups, L<SUP>*</SUP> value increased, but a<SUP>*</SUP> value and b* value decreased. The translucency value measured in the untreated group was statically higher in the AMD groups than in UTML groups (P<0.05). The translucency did not show a significant difference before and after glazing treatment in the UTML group (P>0.05), but significantly decreased compared to the untreated group after glazing treatment in the AMD group (P<0.05). The contrast ratios generally increased after glaze treatment compared to the untreated group. Since the glaze treatment can affect the optical properties of ceramic restorations, the choice of glaze should be considered important for the desired color by the dental technician.

참고문헌 (Reference)

1 김성준, "세라믹 비니어의 글레이징에 따른 반투명도 변화" 대한치과보철학회 53 (53): 138-143, 2015

2 심재훈, "글레이징 처리가 리튬 디실리케이트 글라스 세라믹의 굽힘 강도에 미치는 영향" 대한치과재료학회 46 (46): 185-194, 2019

3 Johnston WM, "Translucency parameter of colorants for maxillofacial prostheses" 8 (8): 79-86, 1995

4 Spyropoulou PE, "Translucency of shaded zirconia core material" 105 (105): 304-307, 2011

5 Matsuzaki F, "Translucency and flexural strength of monolithic translucent zirconia and porcelain-layered zirconia" 34 (34): 910-917, 2015

6 Kosmac T, "The effect of surface grinding and sand blasting on flexural strength and reliability of Y-TZP zirconia ceramic" 15 (15): 426-433, 1999

7 Kerem Yılmaz, "The effect of repeated firings on the color change of dental ceramics using different glazing methods" 대한치과보철학회 6 (6): 427-433, 2014

8 Fairhurst CW, "The effect of glaze on porcelain strength" 8 (8): 203-207, 1992

9 Kosmac T, "The effect of dental grinding and sandblasting on aging and fatigue behavior of dental zirconia(Y-TZP)ceramics" 28 (28): 1085-1090, 2008

10 Denry I, "State of the art of zirconia for dental applications" 24 (24): 299-307, 2008

11 Luthardt RG, "Reliability and properties of ground Y-TZP zirconia ceramics" 81 (81): 487-491, 2002

12 Ban S, "Reliability and properties of core materials for all-ceramic dental restorations" 44 (44): 3-21, 2008

13 Della Bona A, "Optical properties of CAD-CAM ceramic systems" 42 (42): 1202-1209, 2014

14 Elsaka, "Optical and mechanical properties of newly developed monolithic multilayer zirconia" 28 (28): e279-84, 2019

15 Kolakarnprasert N, "New multi-layered zirconias : composition, microstructure and translucency" 35 (35): 797-806, 2019

16 Yamamoto M, "Metal ceramics" Quintessence 219-291, 1985

17 Ueda K, "Light transmittance by a multi-coloured zirconia material" 34 (34): 310-314, 2015

18 Gresnigt M, "Fracture strength, failure type and Weibull characteristics of lithium disilicate and multiphase resin composite endocrowns under axial and lateral forces" 32 (32): 607-614, 2016

19 İblkin Tuncel, "Evaluation of translucency of monolithic zirconia and framework zirconia materials" 대한치과보철학회 8 (8): 181-186, 2016

20 Hamed JG, "Evaluation of biaxial flexural strength and translucency of multichromatic translucent zirconia and lithium disilicate ceramics" 43 (43): 86-93, 2018

21 Subaşı GM, "Effects of Different Glaze Treatments on The Optical Properties and Roughness of Lithium Disilicate Ceramics" 22 (22): 48-55, 2019

22 김희경, "Effect of polishing and glazing on the color and spectral distribution of monolithic zirconia" 대한치과보철학회 5 (5): 296-304, 2013

23 Bayindir F, "Effect of number of firings on the color and translucency of ceramic core materials with veneer ceramic of different thicknesses" 119 (119): 152-158, 2018

24 Shah K, "Effect of coloring with various metal oxides on the microstructure, color, and flexural strength of 3Y-TZP" 87 (87): 329-337, 2008

25 박미경, "Effect of coloring and thickness on the color and translucency parameter of translucent zirconia" 대한치과재료학회 47 (47): 11-22, 2020

26 Piddock V, "Dental ceramics-an update" 18 (18): 227-235, 1990

27 McLean JW, "Dental ceramics, Proceedings of the first international symposium on ceramics" Quintessence Publishing Co., Inc. 83-141, 1983

28 Hugo Lambert, "Dental biomaterials for chairside CAD/CAM: State of the art" 대한치과보철학회 9 (9): 486-495, 2017

29 Sevcan Kurtulmus-Yilmaz, "Comparison of the translucency of shaded zirconia all-ceramic systems" 대한치과보철학회 6 (6): 415-422, 2014

30 Spink LS, "Comparison of an absolute and surrogate measure of relative translucency in dental ceramics" 29 (29): 702-707, 2013

31 Yilmaz C, "Color stability of glazed and polished dental porcelains" 17 (17): 20-24, 2008

32 Nam MG, "Changes in the flexural strength of translucent zirconia due to glazing and lowtemperature degradation" 120 (120): 969-, 2018

33 Guess PC, "All-ceramic system : Laboratory and clinical performance" 55 (55): 333-352, 2011