A Structural Study of the Activated Carbon Fibers as a Function of Activation Degrees

다국어 초록 (Multilingual Abstract)

Isotropic pitch-based carbon fiber was isothermally activated in $CO_2$ atmosphere. Structural parameters of the isotropic carbon fibers and activated carbon fibers (ACFs) were evaluated by X-ray diffraction (XRD). The $d_{002}$ and La of the carbon fibers were measured to be 4.04 ${\AA}$ and 23.6 ${\AA}$ and those of ACFs were 4.29 ${\AA}$ and 22.7 ${\AA}$, respectively, representing less ordered through activation process. The pores in the ACFs were characterized by BET, and they showed super-high specific surface area of maximum value 3,495 $m^2/g$ from average pore size of 8.3 ${\AA}$ at 59% burn-off. It was recognized that 8-9 ${\AA}$ was optimum range of pore size for efficient creation of high specific surface area. The average size of the pores formed at higher temperature ($1100^{\circ}C$) was larger than that of the pores formed at lower temperature ($900^{\circ}C$).