6층겹침ARB공정에 의해 강소성가공된 극저탄소IF강의 어닐링에 따른 미세조직 변화 = Microstructural Evolution with Annealing of Ultralow Carbon IF Steel Severely Deformed by Six-Layer Stack ARB Process

다국어 초록 (Multilingual Abstract)

A sample of ultra low carbon IF steel was processed by six-layer stack accumulative roll-bonding (ARB) and annealed. The ARB was conducted at ambient temperature after deforming the as-received material to a thickness of 0.5 mm by 50% cold rolling. The ARB was performed for a six-layer stacked, i.e. a 3 mm thick sheet, up to 3 cycles (an equivalent strain of ~7.0). In each ARB cycle, the stacked sheets were, first, deformed to 1.5 mm thickness by 50% rolling and then reduced to 0.5 mm thickness, as the starting thickness, by multi-pass rolling without lubrication. The specimen after 3 cycles was then annealed for 0.5 h at various temperatures ranging from 673 to 973 K. The microstructural evolution with the annealing temperature for the 3-cycle ARB processed IF steel was investigated in detail by transmission electron microscopy observation. The ARB processed IF steel exhibited mainly a dislocation cell lamella structure with relatively high dislocation density in which the subgrains were partially observed. The selected area diffraction (SAD) patterns suggested that the misorientation between neighboring cells or subgrains was very small. The thickness of the grains increased in a gradual way up to 873 K, but above 898 K it increased drastically. As a result, the grains came to have an equiaxed morphology at 898 K, in which the width and the thickness of the grains were almost identical. The grain growth occurred actively at temperatures above 923 K.

참고문헌 (Reference)

1 V. M. Segal, 197 : 157-, 1995

2 N. Kamikawa, 55 : 5873-, 2007

3 K. T. Park, 293 : 165-, 2000

4 D. H. Shin, 49 : 2387-, 2000

5 R. Z. Abdulov, 9 : 1445-, 1990

6 Y. Saito, 39 : 1221-, 1998

7 H. W. Kim, 39 : 546-, 2001

8 Y. Saito, 47 : 579-, 1999

9 N. Tsuji, 40 : 795-, 1999

10 S. H. Lee, 46 : 281-, 2002

11 S. H. Lee, 325 : 228-, 2002

12 R. Z. Valiev, 45 : 103-, 2000

13 N. Kamikawa, 5 : 163-, 2004

14 S. H. Lee, 45 (45): 2177-, 2004

15 S. H. Lee, 43 (43): 2320-, 2002

16 이성희, "반복겹침접합압연법에 의해 강소성가공된 무산소동의 미세조직 및 기계적 특성" 한국재료학회 15 (15): 240-245, 2005

17 박영배, "공정 조성 SnPb 솔더의 배선 길이에 따른 electromigration 특성" 한국재료학회 17 (17): 361-365, 2007

18 Cha-Yong Lim, "Formation of Nano-Sized Grains in Cu and Cu-Fe-P Alloys by Accumulative Roll Bonding Process" 대한금속·재료학회 12 (12): 225-230, 2006

19 이성희, "ARB법에 의해 강소성가공된 무산소동의 어닐링 특성" 한국재료학회 15 (15): 555-559, 2005

20 이성희, "ARB법에 의한 인탈산동의 결정립초미세화 및 고강도화" 한국재료학회 16 (16): 592-597, 2006

21 이성희, "ABR 공정에 있어서 미세조직 및 기계적 특성에 미치는 겹침 수의 영향" 대한금속·재료학회 43 (43): 786-792, 2005