Effect of heat treatment on the high cycle fatigue behavior of high strength aluminum alloy 7039 was examined by microcopy, mechanical and fatigue test. The elongated plateshaped grain by the effect of hot rolling and oxide or coarse super hardened pa...
Effect of heat treatment on the high cycle fatigue behavior of high strength aluminum alloy 7039 was examined by microcopy, mechanical and fatigue test. The elongated plateshaped grain by the effect of hot rolling and oxide or coarse super hardened particles, Cr compound(CrAl_7)were observed on the optical microscopy. The density of coarse inherent, θ phase(MgZn_2) was decreased as the time of artificial aging was increased. S1 specimen developed by holding at 480C for 2 hours, holding at room temperature for 72 hours and then aging at 120C for 24 hours was showed the most ex-cellent fatigue limit.