Fe_{60}Sn_{40} 기계적 합금의 구조 및 자기적 특성 연구 = Local Structure and Magnetic Properties of Fe_{60}Sn_{40} Mechanical Alloys

다국어 초록 (Multilingual Abstract)

In this work, we examined the variations in the structural and the magnetic properties of Fe_{60}Sn_{40} mixed powders with the milling time for powders processed by energetic zirconia ball milling for 1, 2, 4, 6, 12, and 24 hours. The structure of mixed powder was examined by using X-ray diffraction (XRD) and the extended X-ray absorption fine structure (EXAFS), and the magnetization was measured by using a vibrating sample magnetometer (VSM). We found that the Fe_{60}Sn_{40} mixed powder was transformed into a metastable Fe_{60}Sn_{40} mechanical alloy by mechanical ball milling. Also, we found that the variation of the magnetization of the mixed powder was closely related to the variation of local structure and that the Fe-Fe ordering in the local structure caused a significant magnetization of the alloys.

국문 초록 (Abstract)

본 연구에서는 지르코니아 볼의 연속적인 충돌에 의하여 1, 2, 4, 6, 12, 24 시간 동안의 기계적 합금화 과정을 거친 Fe_{60}Sn_{40} 혼합 분말의 구조 및 자기적 특성을 조사하였다. 합금화 과정을 거친 혼합 분말의 구조는 XRD 와 EXAFS로 분석 되었고, 각 과정을 거친 시료의 자화는 VSM에 의하여 분석 되었다. 분석 결과 기계적 합금화 과정에서 milling 시간이 증가함에 따라 Fe_{60}Sn_{40} 혼합 분말이 새로운 Fe_{60}Sn_{40} 합금으로 변환되어가는 것을 확인하였고, 혼합분말의 자화의 변화는 국부구조의 변화와 밀접한 관계가 있으며, 국부구조에서 Fe-Fe 결합은 시료의 자화에 중대한 영향을 미치는 것을 확인하였다.

참고문헌 (Reference)

1 J. P. Lei, 15 : 1589-, 2007

2 E. P. Yelsukov, 214 : 258-, 2000

3 D. E. Sayers, 27 : 1204-, 1971

4 B. Ravel, 12 : 537-, 2005

5 양동석, "Fe₆₀Sb₄₀ 기계적 합금의 국부구조분석에 관한 연구" 한국물리학회 62 (62): 492-496, 2012

6 양동석, "Fe60Ti40 기계적 합금의 구조분석 및 자기적 특성에 관한 연구" 한국물리학회 63 (63): 670-673, 2013

7 양동석, "Fe60Co40 기계적 합금의 구조분석 연구" 한국물리학회 60 (60): 658-662, 2010