<P>In this study, the effects of bracket designs and force direction on fracture strength of alumina bracket were evaluated. Two differently designed alumina brackets (MISO, HT Co., Ltd., Seoul, Korea) were tested. Each bracket was bonded with o...
http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
https://www.riss.kr/link?id=A107531518
2007
-
SCOPUS
학술저널
1353-1356(4쪽)
0
상세조회0
다운로드다국어 초록 (Multilingual Abstract)
<P>In this study, the effects of bracket designs and force direction on fracture strength of alumina bracket were evaluated. Two differently designed alumina brackets (MISO, HT Co., Ltd., Seoul, Korea) were tested. Each bracket was bonded with o...
<P>In this study, the effects of bracket designs and force direction on fracture strength of alumina bracket were evaluated. Two differently designed alumina brackets (MISO, HT Co., Ltd., Seoul, Korea) were tested. Each bracket was bonded with orthodontic adhesive to stainless steel cylinder. Compressive force was applied to the tie wing of bracket at 30°, 60°, and 90° to the long axis of the test device. Fracture strengths were assessed by using a universal testing machine (Instron 3366, Instron Co., Ltd., U.S.A.). Fractured bracket surfaces were examined using SEM. Statistical analysis was performed by using SPSS 9.0 for Windows program. Paired samples t-tests and Kruskal-wallis tests were used at P<0.05. The fracture strength ranged from 150 N with the occlusal wing to 63 N with the cervical wing in bracket A. A significant difference was founded in fracture strength between the bracket designs and force directions. Based on this result, it could be concluded that bracket designs and force direction was important rule to improve fracture strength of ceramic bracket.</P>
Combined Effects of Nano-Hydroxyapatite and NaF on Remineralization of Early Caries Lesion
Abrasivity of Desensitizing Dentifrice Containing Sodium Metasilicate
Apatite Forming Ability of a Non-Woven Silica Fabric Containing Calcium