The effects of $Y_2$ $O_3$-substitution on the piezoelectric properties of Pb[(N $i_{1}$3/N $b_{2}$3/)$_{0.15}$(Z $r_{1}$2/ $Ti_{1}$2/)$_{0.85}$] $O_3$ceramics were investigated. It was found that $Y^{3+}$ ions incorporate into Pb-sites of the ceramics, resulting in a increased lattice anisotropy and formation of Pb-vacancies. As a result, an orthorhombic-tetragonal phase transition was induced when $\chi$>0.005. At the morphotropic phase boundary of x=0.005, piezoelectric constants( $k_{p}$, $k_{33}$, and $d_{33}$) showed maximum values of 0.53, 0.58, and 350pC/N, respectively. A 30-layer actuator fabricated with the above material showed a maximum strain of 0.12% under 100V DC bias.