High temperature flow behaviors of Fe-Cr-Mo-V-W-C tool steel were investigated using isothermal compression tests on a Gleeble simulator. The compressive test temperature was varied from 850 to 1,150℃ with the strain rate ranges of 0.05 and 10 s<...
http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
https://www.riss.kr/link?id=A105498608
2018
Korean
KCI등재후보
학술저널
180-186(7쪽)
0
0
상세조회0
다운로드다국어 초록 (Multilingual Abstract)
High temperature flow behaviors of Fe-Cr-Mo-V-W-C tool steel were investigated using isothermal compression tests on a Gleeble simulator. The compressive test temperature was varied from 850 to 1,150℃ with the strain rate ranges of 0.05 and 10 s<...
High temperature flow behaviors of Fe-Cr-Mo-V-W-C tool steel were investigated using isothermal compression tests on a Gleeble simulator. The compressive test temperature was varied from 850 to 1,150℃ with the strain rate ranges of 0.05 and 10 s<sup>-1</sup>. The maximum height reduction was 45%. The dynamic softening related to the dynamic recrystallization was observed during hot deformation. The constitutive model based on Arrhenius-typed equation with the Zener-Hollomon parameter was proposed to simulate the hot deformation behavior of Fe-Cr-Mo-V-W-C steel. An artificial neural network (ANN) model was also developed to compare with the constitutive model. It was concluded that the ANN model showed more accurate prediction compared with the constitutive model for describing the hot compressive behavior of Fe-Cr-Mo-V-W-C steel.
(Received June 18, 2018; Revised June 26, 2018; Accepted July 6, 2018)
참고문헌 (Reference)
1 H. Park, 4 : 116504-, 2017
2 R. Bobbili, 696 : 295-, 2017
3 W. Sha, 28 : 1747-, 2007
4 C. M. Sellars, 14 : 1136-, 1966
5 G. R. Johnson, 541-, 1983
6 H. Y. Li, 557 : 138-, 2013
7 F. J. Zerilli, 61 : 1816-, 1987
8 H. Zhang, 527 : 328-, 2009
9 H. K. D. H. Bhadeshia, 39 : 966-, 1999
10 W. Sha, 28 : 1747-, 2007
1 H. Park, 4 : 116504-, 2017
2 R. Bobbili, 696 : 295-, 2017
3 W. Sha, 28 : 1747-, 2007
4 C. M. Sellars, 14 : 1136-, 1966
5 G. R. Johnson, 541-, 1983
6 H. Y. Li, 557 : 138-, 2013
7 F. J. Zerilli, 61 : 1816-, 1987
8 H. Zhang, 527 : 328-, 2009
9 H. K. D. H. Bhadeshia, 39 : 966-, 1999
10 W. Sha, 28 : 1747-, 2007
11 H. Y. Li, 42 : 192-, 2012
12 K. Singh, 6 : 1-, 2016
13 A. Mirzaei, 24 : 2412-, 2015
14 F. Ren, 24 : 1407-, 2014
15 N. Haghdadi, 49 : 386-, 2013
16 J. Zhao, 92 : 47-, 2014
17 S. Kang, 7 : 12-, 2017
18 C. Zener, 15 : 22-, 1994
19 이운재, "인공 신경망 모델을 활용한 조미니 곡선 예측" 한국열처리공학회 31 (31): 1-5, 2018
20 김근학, "구성 모델과 공정 지도를 이용한 AISI 4340강의 고온 변형 거동" 한국열처리공학회 30 (30): 187-196, 2017
21 박동성, "고합금 공구강의 최적 오스테나이트 처리 온도 결정" 한국열처리공학회 30 (30): 156-163, 2017
22 G. Roberts, "Tool Steel" ASM International 13-, 1998
DLC 박막의 전기전도성, 투과율 및 가스베리어 특성에 관한 연구
학술지 이력
연월일 | 이력구분 | 이력상세 | 등재구분 |
---|---|---|---|
2024 | 평가예정 | 재인증평가 신청대상 (재인증) | |
2021-01-01 | 평가 | 등재학술지 선정 (계속평가) | |
2019-01-01 | 평가 | 등재후보학술지 선정 (신규평가) | |
2018-12-01 | 평가 | 등재후보 탈락 (계속평가) | |
2017-12-01 | 평가 | 등재후보로 하락 (계속평가) | |
2013-01-01 | 평가 | 등재 1차 FAIL (등재유지) | |
2010-01-01 | 평가 | 등재학술지 유지 (등재유지) | |
2008-01-01 | 평가 | 등재 1차 FAIL (등재유지) | |
2005-01-01 | 평가 | 등재학술지 선정 (등재후보2차) | |
2004-01-01 | 평가 | 등재후보 1차 PASS (등재후보1차) | |
2002-07-01 | 평가 | 등재후보학술지 선정 (신규평가) |
학술지 인용정보
기준연도 | WOS-KCI 통합IF(2년) | KCIF(2년) | KCIF(3년) |
---|---|---|---|
2016 | 0.15 | 0.15 | 0.14 |
KCIF(4년) | KCIF(5년) | 중심성지수(3년) | 즉시성지수 |
0.15 | 0.13 | 0.33 | 0.17 |