자기펄스 성형 및 방전 플라즈마 소결 공정으로 제조한 텅스텐 소결체의 특성 = Fabrication and Properties of Densified Tungsten by Magnetic Pulse Compaction and Spark Plasma Sintering

다국어 초록 (Multilingual Abstract)

The present study demonstrates the effect of magnetic pulse compaction and spark plasma sintering on the microstructure and mechanical property of a sintered W body. The relative density of green specimens prepared by magnetic pulse compaction increases with increase in applied pressure, but when the applied pressure is 3.4 GPa or more, some cracks in the specimen are observed. The pressureless-sintered W shows neck growth between W particles, but there are still many pores. The sintered body fabricated by spark plasma sintering exhibits a relative density of above 90 %, and the specimen sintered at 1,600 ℃ after magnetic pulse compaction shows the highest density, with a relative density of 93.6 %. Compared to the specimen for which the W powder is directly sintered, the specimen sintered after magnetic pulse compaction shows a smaller crystal grain size, which is explained by the reduced W particle size and microstructure homogenization during the magnetic pulse compaction process. Sintering at 1,600 ℃ led to the largest Vickers hardness value, but the value is slightly lower than that of the conventional W sintered body, which is attributed mainly to the increased grain size and low sintering density.

참고문헌 (Reference)

1 J. W. Davis, 258-263 : 308-, 1998

2 E. A. Olevsky, 224 : 3177-, 2013

3 J. K. Lee, 118 : 597-, 2006

4 G. Lee, 61 : 22-, 2016

5 I. H. Moon, 102 : 219-, 1984

6 Z. Z. Fang, 53 : 326-, 2008

7 R. M. Raihanuzzaman, 536 : S211-, 2012

8 O. El-Atwani, 528 : 5670-, 2011

9 N. Tamari, 103 : 740-, 1995

10 R. W. Heckel, 221 : 671-, 1961

11 T. E. M. Staab, 11 : 1787-, 1999

12 윤은유, "수분사법으로 제조된 순철 분말의 고압비틀림 성형 공정에 의한 치밀화 및 나노결정화" 한국분말야금학회 18 (18): 411-416, 2011

13 김주훈, "소결조제 변화에 따른 텅스텐카바이드 소결체 특성평가" 한국분말야금학회 26 (26): 132-137, 2019

14 E. Lassner, "Tungsten: Properties, Chemistry, Technology of the Elements, Alloys, and Chemical Compounds" Kluwer Academic/ Plenum Publishers 1999