Changes in the porosity of bulk graphite according to the viscosity of resin for impregnation

다국어 초록 (Multilingual Abstract)

When manufacturing bulk graphite, pores develop within the bulk during the carbonization process due to the volatile components of the fillers and the binders. As a result, the physical properties of bulk graphite are inferior to the theoretical values. Impregnants are impregnated into the pores generated in the carbonization process through pressurization and/or depressurization. The physical properties of bulk graphite that has undergone impregnation and re-carbonization processes are outstanding. In the present study, a green body was manufactured by molding with natural graphite flakes and phenolic resin at 45 MPa. Bulk graphite was manufactured by carbonizing the green body at 700 and it was subsequently impregnated with impregnants having viscosity of 25.0 cP, 10.3 cP, and 5.1 cP, and the samples were re-carbonized at 700°C. The above process was repeated three times. The open porosity of bulk graphite after the final process was 22.25%, 19.86%, and 18.58% in the cases of using the impregnant with viscosity of 25.0 cP, 10.3 cP, and 5.1 cP, respectively.

목차 (Table of Contents)

• Abstract
• 1. Introduction
• 2. Experimental Procedure
• 2.1. Raw materials and preparations
• 2.2. Impregnation
• 2.3. Density and porosity measurement
• 3. Results and Discussion
• 3.1. As carbonized
• 3.2. Impregnation
• 3.3. Density and porosity
• 4. Conclusions
• References