폐콘크리트 및 폐아스콘 순환골재를 이용한 포러스콘크리트의 특성 = Properties of Porous Concrete Using Recycled Aggregates Made from Recycled Concrete and Asphalt Concrete

다국어 초록 (Multilingual Abstract)

The purpose of this study is to ascertain properties of porous concretes (POC) with two types of recycled aggregates. The POC at a water-cement ratio of 18%, void-filling ratios of 30, 50% and recycled coarse aggregate replacements of 0, 10, 20, 30% for natural crushed aggregate are prepared, and tested for compressive and flexural strengths, water permeability, void percentage and water resistance index. From the test results, at void filling ratios of 30% and 50%, the compressive strength reduction of the POC with RA replacement 30% for crushed aggregate is 10% and 20% respectively, in comparison with the POC using crushed aggregate. The coefficient of permeability of POC using recycled aggregates at void filling ratios of 30% and 50 % is 4.08 cm/sec and 2.87 cm/sec, and the continuous void ratio is 32.1% and 26.2% respectively.

국문 초록 (Abstract)

본 연구는 폐콘크리트 및 폐아스콘 순환골재를 이용한 포러스콘크리트의 특성을 파악하기 위해, 물시멘트비 18%, 공극충전율 30 및 50%, 그리고 순환골재 치환율 0, 10, 20, 및 30%로 한 폐콘크리트 및 폐아스콘 순환골재 POC를 제작하여 그 강도특성, 투수성, 공극특성 및 내수성 지수를 검토하였다. 그 결과, 폐콘크리트 및 폐아스콘 순환골재를 이용한 POC 강도는 공극충전율에 관계 없이 순환골재 치환율의 증가와 함께 감소하였다. 그리고 폐콘크리트 순환골재 치환율 30%를 이용한 POC의 보통 부순골재 POC에 대한 압축강도 감소율은 공극충전율 30%에서 10%, 공극충전율 50%에서 20%로 나타났다. 폐콘 및 폐아스콘 순환골재를 이용한 POC의 공극충전율 30% 및 50%에서의 투수계수는 평균적으로 4.08cm/sec 및 2.87cm/sec로 각각 나타났으며, 그 연속공극률은 32.1% 및 26.2%로 각각 나타났다. 추후 순환골재 POC의 강도 및 내수성 지수의 개선에 대한 대책이 요구된다.

참고문헌 (Reference)

1 이욱재, "폐아스콘을 함유한 재생콘크리트의 강도발현 특성평가" 16 (16): 205-208, 2004

2 백성현, "재생골재를 이용한 투수콘크리트의 특성" 17 (17): 437-440, 2005

3 出村克宣, "ポリマー混入透水コンクリートの開発" 47 : 226-231, 1993

4 Wan-Ki Kim, "Effects of Silica Fume and Polypropylene Fiber Additives Affecting Strength Properties of Permeable Polymer-Modified Concretes" 26-29, 1999