폐석회석을 이용하여 단열블록 제조 시 열전도에 미치는 영향인자 분석

다국어 초록 (Multilingual Abstract)

An insulating brick was developed and evaluated as a potential recycling Waste Limestone (WL) with Melting Slag (MS). We aimed at analyzing the parameters affecting the insulating brick manufacture to enhance the recyclability of WL. In this study, The thermal conductivity, compressive strength and apparent porosity of prepared brick were measured with the addition of aluminum dross and the molar ratio of the alkali activator. The thermal conductivity, compressive strength and apparent porosity were 0.28 W/mK, 2.41 MPa and 44.72% respectively at a mixing ratio of 9.5 : 0.5wt%, 1.5 M SiO2/Na2O, 3wt% aluminum dross. Thus, it met the standards of insulating fire bricks (KS L 3301).

목차 (Table of Contents)

• I. 서 론
• II. 재료 및 방법
• 1. 실험재료
• 2. 실험조건 및 실험방법
• 3. 분석항목
• III. 결과 및 고찰
• 1.폐석회석, 용융슬래그 혼합비 영향
• 2.반응조건에 따른 기공율 평가
• 3. 알칼리 활성화제 몰비별, 알루미늄 드로스 첨가량별단열블록의 특성
• IV. 결 론
• 사 사
• References

참고문헌 (Reference)

1 최수철, "광미와 용융슬래그를 이용한 지오폴리머 제조시 CaO와 Fe2O3의 영향" 한국폐기물자원순환학회 30 (30): 572-577, 2013

2 오아람, "광물 찌꺼기를 이용한 지오폴리머 폼 블록 제조시 SiO2/Na2O의 몰비의 영향" 한국폐기물자원순환학회 29 (29): 155-160, 2012

3 Yip, C. K., "The coexistence of geopolymeric gel and calcium silicate hydrate at the early stage of alkaline activation" 42 : 1688-1697, 2005

4 Khalil, K. M. S., "Preparation and characterization of thermally stable porous ceria aggregates formed via a sol-gel process of ultrasonically dispersed cerium (IV) isopropoxide" 78 (78): 83-89, 2005

5 Rhee, S. K., "Porosity-thermal conductivity correlations for ceramic materials" 20 : 89-93, 1975

6 "Ministry of Environment : Environmental statistics yearbook"

7 Choi, B. H, "Hydrothermal reaction characteristics on the ALC of pitchstone-lime system (II) - Effect of the various gelling and curing conditions" 31 (31): 194-200, 1994

8 Yip, C. K., "Effect of calcium silicate sources on geopolymerisation" 38 : 554-564, 2008

9 Levy, F. L., "A modified maxwell-eucken equation for calculating the thermal conductivity of twocomponent solutions or mixtures" 4 (4): 223-225, 1981