<P>Zinc oxide(ZnO) has been widely applied in the fields of cosmetics, paint, coating and gas sensor. Size down of ZnO is essential for the preparation of sol or film of ZnO in the application. The size and shape of ZnO particles are controlled ...
http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
https://www.riss.kr/link?id=A107602418
2009
-
SCOPUS
학술저널
461-464(4쪽)
0
상세조회0
다운로드다국어 초록 (Multilingual Abstract)
<P>Zinc oxide(ZnO) has been widely applied in the fields of cosmetics, paint, coating and gas sensor. Size down of ZnO is essential for the preparation of sol or film of ZnO in the application. The size and shape of ZnO particles are controlled ...
<P>Zinc oxide(ZnO) has been widely applied in the fields of cosmetics, paint, coating and gas sensor. Size down of ZnO is essential for the preparation of sol or film of ZnO in the application. The size and shape of ZnO particles are controlled by varying drying method. The ZnO was prepared by mixing of zinc acetate and sodium hydroxide at 0°C. Then it was freeze dried or 20°C vacuum dried. After washing the residual ions, it was further compared by drying at 20°C vacuum drying or 200 °C oven drying. The ZnO powder was characterized by XRD, Brunauer-Emmet-Teller analysis(BET) and transmission electron microscope(TEM). The ZnO have wurzite structure with ~10 nm particle size when it was prepared by freeze drying and then 20°C vacuum drying after washing the residual ions. On the other hand, without freeze drying, the ZnO particles observed to be aggregated to 200~400 nm with primary particle size of ~20 nm. The smaller size of ZnO particle in freezing drying compared to 20°C vacuum drying may be explained by frozen water preventing the growth of ZnO particles.</P>
Effects of Flow Characteristics in Polymer Electrolyte Membrane Fuel Cell
Synthesis of Zeolite Added Clay and Sewage Sludge