인가 자기장에 의한 YBCO 초전도체 복합체의 포획 자기장 특성 = The Trapped Field Characteristics of YBCO Superconductor Composite in Terms of Applied Magnetic Field

다국어 초록 (Multilingual Abstract)

We have measured the trapped field of YBCO bulk with different configuration by applying the magnetic field of $Nb_3Sn$ superconducting magnet. Initially the circular type of YBCO bulk superconductor was prepared and then hole, parallel to the c-axis and located at the center of bulk was mechanically drilled. The YBCO bulk with hole was filled with resin. Typical size of hole in YBCO bulk was 10 mm in diameter. Trapped field characteristics were compared with different specimen conditions. Our preliminary result indicates the increment rate of trapped field, 0.232 kG, measured on the YBCO without hole was much higher than that, 0.011 kG, measured on YBCO with hole.

참고문헌 (Reference)

1 G. E. Jang, "The effect of impregnation by resin and CNT compound on the mechanical and magnetic properties of YBCO superconductor" 468 : 1411-1414, 2008

2 M. Tomita, "Reliability of mechanical properties for bulk superconductors with resin impregnation" 378 : 783-787, 2002

3 M. Murakami, "Melt-processed light rare earth element-Ba-Cu- O" 9 : 1015-, 1996

4 H. Fujimoto, "Melt processing of YBaCuO oxide superconductors" 2 : 285-, 1990

5 M. Tomita, "High-temperature superconductor bulk magnets that can trap magnetic fields of over 17 tesla at 29 K" 421 : 517-520, 2003

6 M. Tomita, "Effect of resin layer on the thermal stress of bulk superconductors" 392 : 493-498, 2003

7 Y. Ren, "Damage caused by magnetic pressure at high trapped field in quasi-permanent magnets composed of melt-textured Y-Ba-Cu-O superconductor" 251 : 15-, 1995

8 M. Murakami, "A New Process with the Promise of High $J_c$ in Oxide Superconductor" 28 : 1189-1194, 1989