Barium ferrite (BaFe<SUB>12</SUB>O<SUB>19</SUB>) powders were synthesized by the co-precipitation method. Fe<SUP>3+</SUP>: Ba<SUP>2+</SUP> mole ratio was fixed 8 and relative amount of Fe<SUP>3+<...
http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
https://www.riss.kr/link?id=A82393363
2010
Korean
428
KCI등재,ESCI
학술저널
134-142(9쪽)
0
0
상세조회0
다운로드다국어 초록 (Multilingual Abstract)
Barium ferrite (BaFe<SUB>12</SUB>O<SUB>19</SUB>) powders were synthesized by the co-precipitation method. Fe<SUP>3+</SUP>: Ba<SUP>2+</SUP> mole ratio was fixed 8 and relative amount of Fe<SUP>3+<...
Barium ferrite (BaFe<SUB>12</SUB>O<SUB>19</SUB>) powders were synthesized by the co-precipitation method. Fe<SUP>3+</SUP>: Ba<SUP>2+</SUP> mole ratio was fixed 8 and relative amount of Fe<SUP>3+</SUP> and Ba<SUP>2+</SUP> was controlled. The effects of the pH (= 8, 9, 10), calcination temperature and time on the morphology, structure and magnetic properties of the barium ferrite particles are characterized using XRD, FESEM, and VSM respectively. Coercivity and magnetization value of powders were changed with calcination temperature and time, relative amount of Fe<SUP>3+</SUP> and Ba<SUP>2+</SUP> and pH. Single-phase barium ferrite was obtained when pH value was 9 in the investigated range of Fe<SUP>3+</SUP>: Ba<SUP>2+</SUP> relative amount and secondary phases were appeared at Fe<SUP>3+</SUP>: Ba<SUP>2+</SUP> relative amount of 14.4 : 1.8. The largest value of magnetization (65.7 emu/g) was obtained when Fe<SUP>3+</SUP>: Ba<SUP>2+</SUP> mole ratio was 12.8 : 1.6 and calcination temperature was 900 ℃ with air calcination atmosphere. The largest value of coercivity (5280 Oe) was obtained with O₂ calcination atmosphere.
참고문헌 (Reference)
1 X. Liu, 195 : 452-, 1999
2 V. B. Bregar, 40 : 1679-, 2004
3 M. El-Hilo, 129 : 339-, 1994
4 H. Sozeri, 321 : 2717-, 2009
5 H. Sakai, 28 : 3355-, 1992
6 S. E. Jacobo, 32 : 1025-, 1997
7 H. S. Shin, 34 : 1045-, 1997
8 U. Topal, 428 : 17-, 2007
9 S. R. Janasi, 238 : 168-, 2002
10 M. Radwan, 181 : 106-, 2007
1 X. Liu, 195 : 452-, 1999
2 V. B. Bregar, 40 : 1679-, 2004
3 M. El-Hilo, 129 : 339-, 1994
4 H. Sozeri, 321 : 2717-, 2009
5 H. Sakai, 28 : 3355-, 1992
6 S. E. Jacobo, 32 : 1025-, 1997
7 H. S. Shin, 34 : 1045-, 1997
8 U. Topal, 428 : 17-, 2007
9 S. R. Janasi, 238 : 168-, 2002
10 M. Radwan, 181 : 106-, 2007
11 M. M. Rashad, 453 : 304-, 2008
12 H. F. Yu, 416 : 222-, 2006
13 S. R. Janasi, 185 : 479-, 2001
14 D. Mishra, 86 : 132-, 2004
15 T. Fujiwara, 21 : 1480-, 1985
16 X. Liu, 184 : 344-, 1998
17 J. Matutes-Aquino, 42 : 295-, 2000
18 S. E. Jacobo, 260 : 37-, 2003
19 O. Abe, 101 : 103-, 1997
20 G. Xu, 301 : 383-, 2006
21 K. K. Mallick, 27 : 2045-, 2007
22 배철훈, "세라믹 제조공정, (ITC 2003)"
23 백인승, "공침법으로 합성한 바륨 페라이트(BaM)의 형성과 자기적 성질에 미치는 금속이온 몰 비 및 pH와 열처리 조건의 영향" 한국자기학회 19 (19): 209-215, 2009
24 V. Pillai, "Colloids Surf. A: Physicochem" 80 : 69-, 1993
엑스선 공명 자기 산란을 이용한 자성 다층박막 및 나노 구조체의 자기 구조와 자기 스위칭 메커니즘의 연구
평판형 전자기 엑츄에이터의 집중매개변수 모델링 및 해석
학술지 이력
연월일 | 이력구분 | 이력상세 | 등재구분 |
---|---|---|---|
2027 | 평가예정 | 재인증평가 신청대상 (재인증) | |
2021-01-01 | 평가 | 등재학술지 유지 (재인증) | |
2018-01-01 | 평가 | 등재학술지 유지 (등재유지) | |
2015-01-01 | 평가 | 등재학술지 유지 (등재유지) | |
2011-01-01 | 평가 | 등재학술지 유지 (등재유지) | |
2009-01-01 | 평가 | 등재학술지 유지 (등재유지) | |
2007-01-01 | 평가 | 등재학술지 유지 (등재유지) | |
2005-01-01 | 평가 | 등재학술지 유지 (등재유지) | |
2002-07-01 | 평가 | 등재학술지 선정 (등재후보2차) | |
2000-01-01 | 평가 | 등재후보학술지 선정 (신규평가) |
학술지 인용정보
기준연도 | WOS-KCI 통합IF(2년) | KCIF(2년) | KCIF(3년) |
---|---|---|---|
2016 | 0.13 | 0.13 | 0.11 |
KCIF(4년) | KCIF(5년) | 중심성지수(3년) | 즉시성지수 |
0.11 | 0.12 | 0.299 | 0.05 |