This study was performed to evaluate void ratio, compressive and flexural strength, and pH properties according to the admixture ratio of rice husk ash, aggregate size, and neutral treatment time of porous concrete with an admixture of rice husk ash p...
This study was performed to evaluate void ratio, compressive and flexural strength, and pH properties according to the admixture ratio of rice husk ash, aggregate size, and neutral treatment time of porous concrete with an admixture of rice husk ash produced as an agricultural by-product. The SEM results for cement mortar with a 5% rice husk ash admixture for the weight of cement formed more C-S-H hydrates due to the SiO₂ present in the applied rice husk ash. According to the results of the SEM test, the SiO₂ that was a major chemical element of rice husk ash generated a large amount of calcium hydroxide in the early stage of the hydration process of cement leading to the formation of ettringite. The void ratio of porous concrete with an admixture of rice husk ash decreased with increasing admixture ratio of rice husk ash. In addition, the void ratio of porous concrete with an admixture of rice husk ash decreased compared to porous concrete with no admixture of rice husk ash. The compressive and flexural strength of porous concrete with a 5% and 10% admixture ratio of rice husk ash slightly increased compared to concrete with no admixture of rice husk ash. The pH value of porous concrete rapidly decreased immediately after neutral treatment. Then, it gradually increased and decreased again after 14 days. Also, for neutral treatment, the pH value of porous concrete showed appropriate pH levels(less than 9.5) in all mixtures for planting at 28 curing days.